Thermally reactive ink transfer system
View Patent ↗An ink transfer system including an ink transfer decal that is transferable to a final substrate, such as a bare metal or pre-painted autobody part, without use of a separate adhesive. The transferred ink decal is capable of withstanding temperature elevations common during automotive paint baking without significant thermal degradation, discoloration, shrinkage or pealing.
1. A method of creating and transferring a solid ink design to a substrate comprising the steps of:
(a) providing a decal that does not include a separately applied adhesive, said decal comprising
(i) a flexible backing sheet having a surface adapted to releaseably receive polymer resins,
(ii) an ink transfer coating comprising one or more ink layers and, optionally, a transparent base coat, each of said one or more ink layers and optional base coat being printed onto said sheet as a liquid comprising a thermoplastic polymer resin, a UV stabilizer to inhibit photo degradation of polymers formed from said resin, an antioxidant to inhibit oxidative degradation of polymers formed from said resin, and a solvent system, said liquid from which any of said one or more ink layers and optional base coat are formed being capable of drying on said sheet by solvent evaporation upon being allowed to dry for one hour at ambient conditions, and
(iii) a removable transfer medium coating deposited upon said dried ink transfer coating to form a film that will not strongly adhere to said ink transfer coating;
(b) removing said flexible backing sheet from said decal to expose a surface of said ink transfer coating and applying said exposed surface to said substrate; and
(c) stripping said transfer medium coating from said ink transfer coating with said ink transfer coating remaining on said substrate.
2. The method according to claim 1 , said flexible backing sheet comprising water slide decal paper.
3. The method according to claim 2 , step (b) including wetting said backing sheet prior to removing said backing sheet from said decal.
4. The method according to claim 3 , step (b) including removing excess moisture from between said ink transfer coating and said substrate.
5. The method according to claim 4 , step (b) including drying substantially all surface moisture from said decal.
6. The method according to claim 1 , said ink transfer coating including an ink layer and a base coat.
7. The method according to claim 6 , the margins of said ink layer being included entirely within the margins of said base coat.
8. The method according to claim 1 , said method further comprising:
(d) applying a clear coat over said substrate and said ink transfer coating after step (c) with no raised transition between said substrate and said ink transfer coating being perceptible to the touch or to the naked eye after said clear coat application.
9. The method according to claim 8 , after step (d), baking said clear coat at a temperature of between 250 to 325° F. thereby fusing said ink transfer coating to said substrate and said clear coat.
10. The method according to claim 1 , said substrate being a surface of a vehicle or vehicle accessory.
11. The method according to claim 10 , said substrate being pre-painted prior to application of said decal.
12. The method according to claim 1 , said substrate being a flat surface.
13. The method according to claim 12 , further comprising:
(e) bending, stamping or otherwise shaping said substrate surface after application of said decal thereby causing said ink transfer coating to stretch and elongate without cracking.
14. The method according to claim 1 , said surface being a contoured surface.
15. The method according to claim 14 , further comprising:
(f) stretching said decal over said contoured surface after removing said backing sheet without wrinkling or damaging the decal.
16. A method of creating and transferring a solid ink design to a substrate comprising the steps of:
(a) creating a decal that does not include a separately applied adhesive by
(i) applying an ink transfer coating comprising one or more ink layers and, optionally, a transparent base coat to a flexible backing sheet having a surface adapted to releasably receive polymer resins, each of said one or more ink layers and optional base coat being printed onto said sheet as a liquid comprising a thermoplastic polymer resin, a UV stabilizer to inhibit photo degradation of polymers formed from said resin, an antioxidant to inhibit oxidative degradation of polymers formed from said resin, and a solvent system, each of said one or more ink layers and optional base coat capable of drying on said sheet by solvent evaporation upon being allowed to dry for one hour at ambient conditions, and
(iii) depositing a removable transfer medium coating upon said dried ink transfer coating to form a film that will not strongly adhere to said ink transfer coating;
(b) removing said flexible backing sheet from said decal to expose a surface of said ink transfer coating and applying said exposed surface to said substrate; and
(c) stripping said transfer medium coating from said ink transfer coating with said ink transfer coating remaining on said substrate.
17. The method according to claim 16 , said ink transfer coating including an ink layer and a base coat.
18. The method according to claim 16 , the margins of said ink layer being included entirely within the margins of said base coat.
19. The method according to claim 16 , further comprising:
(d) applying a clear coat over said substrate and said ink transfer coating with no raised transition between said substrate and said ink transfer coating being perceptible to the touch or to the naked eye after said clear coat application.
20. The method according to claim 16 , said substrate being a surface of a vehicle or vehicle accessory.
21. The method according to claim 20 , said substrate being pre-painted prior to application of said decal.
22. The method according to claim 16 , said substrate being a flat surface.
23. The method according to claim 22 , further comprising:
(e) bending, stamping or otherwise shaping said substrate surface after application of said decal thereby causing said ink transfer coating to stretch and elongate without cracking.
24. The method according to claim 16 , said surface being a contoured surface.
25. The method according to claim 24 , further comprising:
(f) stretching said decal over said contoured surface after removing said backing sheet without wrinkling or damaging the decal.
26. The method according to claim 19 , after step (d), baking said clear coat at a temperature of between 250 to 325° F. thereby fusing said ink transfer coating to said substrate and said clear coat.
27. The method according to claim 16 , said flexible backing sheet being water slide decal paper.