Method of increasing the absorption rate of peroxides into polymer particles
View Patent ↗The present invention provides a method of increasing the absorption rate of peroxides into polymer particles used to fabricate electrical cable insulation. The method includes contacting the polymer particles with a peroxide compound and an additive under physical mixing conditions at a temperature that is above the melting point of the peroxide compound but below the softening point of the polymer particles for a period of time sufficient to allow the peroxide compound to absorb into the polymer particles. Preferably, the additive is squalane or another branched, hydrocarbon oil that substantially increases the rate at which the peroxide compound is absorbed into the polymer particles and improves the peroxide cure.
1. A method of fabricating insulated electrical cable, comprising:
providing polymer particles that have absorbed a peroxide compound and an absorption-promoting additive comprising a branched, hydrocarbon oil, wherein the weight ratio of the peroxide compound to the absorption-promoting additive is within the range of from about 1:1 to about 40:1;
melting the peroxide-containing polymer particles in a screw feed and coaxially extruding the molten peroxide-containing polymer onto a wire conductor or wire bundle; and
passing the polymer-coated wire conductor or wire bundle through a catenary heated to a temperature sufficient to cause the peroxide in the extruded polymer to decompose and thereby cross-link the polymer.
2. The method according to claim 1 wherein the peroxide compound is dicumyl peroxide.
3. The method according to claim 1 wherein the absorption-promoting additive is squalane.
4. The method according to claim 1 wherein the absorption-promoting additive is a polybutene having a weight average molecular weight within the range of from about 300 to 1000.
5. The method according to claim 1 wherein the absorption-promoting additive is light mineral oil or heavy mineral oil.
6. The method according to claim 1 wherein the polymer particles comprise ethylene-propylene rubber.
7. The method according to claim 1 wherein the weight ratio of the peroxide compound to the absorption-promoting additive is within the range of from about 3:2 to about 15:2.
8. The method according to claim 1 wherein the peroxide compound and the absorption-promoting additive are pre-mixed together prior to being absorbed into the polymer particle.
9. The method according to claim 8 wherein the pre-mixed peroxide compound and absorption-promoting additive are heated until a homogenous liquid is obtained before being absorbed into the polymer particles.
10. The method according to claim 1 wherein the peroxide compound is dicumyl peroxide and wherein the absorption-promoting additive is squalane.
11. The method according to claim 10 wherein the amount of dicumyl peroxide absorbed into the polymer particle is from about 0.5% to about 2% by weight of the polymer particles.
12. The method according to claim 10 wherein the weight ratio of the dicumyl peroxide to the squalane is within the range of from about 3:2 to about 15:2.
13. A composition for use in forming electrical insulation on a conducting wire comprising polymer particles that have absorbed a peroxide compound and an absorption-promoting additive comprising a branched, hydrocarbon oil, wherein the weight ratio of the peroxide compound to the absorption-promoting additive is within the range of from about 1:1 to about 40:1.
14. The composition according to claim 13 wherein the peroxide compound is dicumyl peroxide.
15. The composition according to claim 13 wherein the absorption-promoting additive is squalane.
16. The composition according to claim 13 wherein the peroxide compound is dicumyl peroxide and wherein the absorption-promoting additive is squalane.
17. The composition according to claim 16 wherein the amount of dicumyl peroxide absorbed into the polymer particles is from about 015% to about 2% by weight of the polymer particles.
18. The composition according to claim 16 wherein the weight ratio of the dicumyl peroxide to the squalane is within the range of from about 3:2 to about 15:2.