View Patent ↗The invention relates to pulverulent core/shell polymers for the preparation of a plastisol, which have surprisingly low water absorption. The invention further relates to the plastisol pastes which are prepared from these polymers and likewise have low water absorption and additionally possess good storage stability, good mechanical properties and good plasticizer compatibility. The core/shell polymers consist of latex particles having a primary particle size of at least 250 nm, the core consisting of methyl methacrylate, (meth)acrylic esters with C 2 to C 8 or aromatic alcohol radicals and optionally further monomers, and the shells(s) comprising, in addition to these components, also amides of (meth)acrylic acid and/or amine-substituted alkyl esters of (meth)acrylic acid.
1. A core/shell polymer consisting of:
latex particles having a primary particle size of at least 250 nm,
the core consisting of
a) 20-85 mol % of methyl methacrylate,
b) 15-80 mol % of (meth)acrylic ester whose alcohol component contains 2-8 carbon atoms or an aromatic radical, and
c) 0-30 mol % of further copolymerizable monomers, excluding N-containing compounds,
wherein a), b) and c) together add up to 100 mol %, and
at least one shell consisting in each case of
a′) 20-79.5 mol % of methyl methacrylate,
b′) 15-79.9 mol % of (meth)acrylic ester whose alcohol component contains 3-8 carbon atoms or an aromatic radical,
c′) 0.3-10 mol % of a compound selected from the group consisting of acrylamide, methacrylamide, N-methyl(meth)acrylamide, N-dimethylaminoethyl(meth)acrylamide, N-dimethylaminopropyl(meth)acrylamide, N-isopropyl(meth)acrylamide, N-tert-butyl(meth)acrylamide, N-isobutyl(meth)acrylamide, N-decyl(meth)acrylamide, N-cyclohexyl(meth)acrylamide, N-1,3-(dimethylamino)-2,2-dimethylpropyl)methacrylamide, N-dodecyl(meth)acrylamide, N-[3-dimethylaminopropyl](meth)acrylamide, N-methacryloylmorpholine, N-methacryloyl-2-pyrrolidinone and mixtures thereof, and
d′) 0-30 mol % of further copolymerizable monomers, wherein
a′), b′), c′) and d′) of one shell in each case add up to 100 mol %, and
component d′) of at least one shell consists of less than 0.5 mol % of a monomer having a carboxyl group or a sulphonic acid group or a phosphonic group and optionally further copolymerizable monomers.
2. The core/shell polymer according to claim 1 , wherein the latex particles consist of a core and a shell in a weight ratio of core to shell between 10:90 and 90:10.
3. The core/shell polymer according to claim 1 , wherein the core has two shells having identical or different monomer compositions.
4. The core/shell polymer according to claim 1 , wherein component b) of the core is n-butyl(meth)acrylate, i-butyl(meth)acrylate, t-butyl(meth)acrylate or a mixture thereof.
5. The core/shell polymer according to claim 1 , wherein both component b) of the core and component b′) of at least one shell is n-butyl(meth)acrylate, i-butyl(meth)acrylate, t-butyl(meth)acrylate or a mixture thereof.
6. The core/shell polymer according to claim 1 , wherein the water absorption of the polymer is less than 3.0%.
7. A plastisol comprising a core/shell polymer according to claim 1 and at least one plasticizer.
8. The plastisol according to claim 7 , wherein at least one of the plasticizers is a dialkyl phthalate.
9. A process for preparing a plastisol comprising a core/shell polymer according to claim 1 , wherein
a) the core/shell polymer is prepared by emulsion polymerization which may be multistage, to obtain a dispersion,
b) the dispersion is dried, and
c) subsequently admixed with at least one plasticizer and optionally with adhesion promoters and/or fillers and optionally further constituents customary for plastisols.
10. The process according to claim 9 , comprising admixing 100 parts by weight of the core/shell polymer with
50-300 parts by weight of a plasticizer, 40-120 parts by weight of an adhesion promoter and/or 0-300 parts by weight of fillers.
11. The process according to claim 9 , wherein the dispersion is dried by spray-drying.
12. A method of protecting or sealing an article, comprising:
contacting said article with the plastisol of claim 7 .
13. The core/shell polymer according to claim 1 , wherein the water absorption of the polymer is less than 2.0%.