Method for the production of membrane/electrode units
View Patent ↗The invention relates to a method for production of a membrane/electrode unit, whereby a conducting polymer membrane is compressed with two electrodes until a given compression is achieved. Said method permits an increase in resting voltage of the membrane/electrode unit in use, the amount of damage during production is reduced and a constant thickness within a production run is achieved.
1. A method for the production of a membrane electrode unit comprising the steps of:
providing one or more proton conductive polymer membranes, each of the membranes having a thickness, at least one polymer membrane is doped with at least one mineral acid, said at least one polymer of said membrane having at least one basic hetero atom, said basic hetero atom is selected from the group consisting of: O, S, and/or N;
providing two or more electrodes;
compressing said proton conductive polymer membrane with said electrodes;
wherein the compressing step is carried out until a presettable compression within the range of 1 to 40% is achieved and the thickness of the proton conductive polymer membrane is reduced.
2. The method according to claim 1 , wherein the compressing step is carried out at an elevated temperature.
3. The method according to claim 1 , wherein said presettable compression is achieved within a period of 1 to 100 seconds.
4. The method according to claim 1 , wherein the compressing step is carried out at a compression speed in the range of 0.2 to 20%/s.
5. The method according to claim 1 , wherein one or more previously compressed said membrane electrode units are further compressed in another process.
6. The method according to claim 1 , wherein said membrane electrode unit further comprising:
providing at least two electrodes, wherein at least one of the electrodes having a catalyst; said catalyst containing at least one precious metal is selected from the group consisting of: a member of the platinum group, Au, Ag; a member of the platinum group and Au; a member of the platinum group and Ag; or Au and/or Ag.
7. The method according to claim 1 , wherein said polymer membrane is an alkaline polymer with at least one nitrogen atom in a repeating unit with at least one nitrogen atom.
8. The method according to claim 1 , wherein said polymer membrane is an alkaline polymer having at least one aromatic ring with at least one nitrogen atom.
9. The method according to claim 1 , wherein said polymer membrane is selected from the group consisting of: a polyimidazole, a polybenzimidazole, a polybenzothiazole, a polybenzoxazole, a polytriazole, a polyoxadiazole, a polythiadiazole, a polypyrazole, a polyquinoxaline, a poly(pyridine), a poly(pyrimidine), or a poly(tetrazapyrene).
10. The method according to claim 1 , wherein said polymer membrane is comprised of a mixture comprising one or more alkaline polymers and one additional polymer.
11. The method according to claim 9 wherein said mineral acid is selected from the group consisting of phosphoric acid, sulphuric acid, or phosphoric acid and sulphuric acid.
12. The method according to claim 1 , characterized in that said polymer membrane is comprised of para-polybenzimidazoles.
13. The method according to claim 6 , wherein said catalyst is applied to said polymer membrane.
14. The method according to claim 6 , wherein said catalyst having a thickness in the range of from 0.1 to 50 μm.
15. The method according to claim 6 , wherein said catalyst is comprised of catalytically active particles having a size in the range of from 5 to 200 nm.
16. The method according to claim 6 , wherein said catalyst is comprised of catalytically active particles on a support; said catalytically active particles ranging in size from 1 to 20 nm.
17. The method according to claim 6 , wherein said electrodes is comprised of 0.1 to 10 g/m 2 of a catalytically active substance.
18. The method according to claim 6 , wherein the weight ratio of the precious metals of the platinum group, Au, or Ag (i) to the metals less precious according to the electrochemical series (ii) is between 1:100 to 100:1.
19. The method according to claim 1 further comprising the use of one or more presses.
20. The method according to claim 1 wherein the presettable compression being with the range of 15-40%.
21. The method according to claim 1 wherein the presettable compression being with the range of 15-25%.