Method for forming a conversion layer on an aluminum alloy product prior to fluxless brazing
View Patent ↗A method of assembling aluminum alloy products, such as sheets, strips or tubes, by means of fluxless brazing, where the absence of flux is made possible by using a prior treatment resulting in formation of a conversion layer on the surface of the products. The treatment involves using a solution containing K + and F − ions and at least one acid in a quantity such that the pH of the solution is less than 3. The inventive method enables effective flux was brazing in industrial conditions, such as a for the production of heat exchangers used in motor vehicles.
1. In a method for assembling aluminum alloy sheets, strips or tubes of heat exchangers by fluxless brazing,
the improvement comprising a surface pretreatment comprising subjecting the tubes, strips or sheets to a solution containing K + and F − ions and at least one acid in an amount sufficient that the solution has a pH less than 3, without addition of hydrofluoric acid to the solution, wherein the K + and F − ions are added to the solution in the form of a mixture comprising KCl +NH 5 F 2 ,
to form thereby a conversion layer over at least part of the surface of the tubes, strips or sheets,
the conversion layer enabling brazing in the absence of flux.
2. Method as claimed in claim 1 , additionally comprising a step of alkaline dipping prior to the surface pretreatment.
3. Method as claimed in claim 1 , wherein the acid is sulfuric acid in a concentration of 10 to 40 g/l.
4. Method as claimed in claim 1 , wherein the surface pretreatment is performed at a temperature of between 30 and 100° C.