Aqueous silane nanocomposites
View Patent ↗The present invention provides a composition based on the reaction at least of the following components: (i) a glycidyloxypropylalkoxysilane, (ii) an aqueous silica sol having an SiO 2 content of >20% by weight, (iii) an organic acid hydrolysis catalyst, and (iv) n-propyl zirconate, butyl titanate or titanium acetylacetonate as crosslinker, a process for its preparation, and the use thereof, particularly as a composition for scratch resistant coatings, and also provides articles thus coated.
1. A storage stable composition, comprising:
the reaction products of
3-glycidyloxypropyltrimethoxysilane;
a colloidally disperse silica sol having a pH of 3-5 and a solids content of greater than 20 to 50% by weight;
at least one of acetic acid and maleic acid; and
n-propyl zirconate;
wherein
a mean particle diameter of particles of the silica sol is from 40 to 200 nm,
a flash point of the composition is 90° C. or higher,
a chloride content of the composition is less than 0.8% by weight, and
the composition is obtained by hydrolysis and further reaction of a mixture comprising:
(i) 3-glycidyloxypropyltrimethoxysilane,
(ii) the colloidally disperse silica sol,
(iii) an organic acid hydrolysis catalyst selected from the group consisting of acetic acid and maleic acid, and
(iv) n-propyl zirconate as crosslinker;
followed by distillation of alcohol resulting from hydrolysis.
2. The storage stable composition as claimed in claim 1 , wherein a content of the n-propyl zirconate is from 0.5 to 8% by weight based on the entire composition.
3. The storage stable composition as claimed in claim 1 , wherein the reaction mixture further comprises at least one silane selected from the group consisting of a tetraalkoxysilane, an alkylsilane and a phenyltrialkoxysilane as a component (v).
4. The storage stable composition as claimed in claim 1 , wherein a solids content is from greater than 40 to less than 60% by weight, based on the overall composition.
5. The storage stable composition as claimed in claim 1 , wherein a content of hydrolysis alcohol is less than 5% by weight, based on the overall composition.
6. The storage stable composition as claimed in claim 1 , further comprising from 5 to 10% by weight of 1-methoxy-2-propanol, based on the overall composition.
7. The storage stable composition as claimed in claim 1 , wherein a content of water is from 30 to 70% by weight, based on the overall composition.
8. The storage stable composition as claimed in claim 1 , further comprising at least one surfactant.
9. The storage stable composition as claimed in claim 1 , further comprising a hydrosil system.
10. The storage stable composition as claimed in claim 1 , further comprising a diluent, wherein the diluent is water or 1-methoxy-2-propanol.
11. The storage stable composition as claimed in claim 1 , hydrolysis reaction is conducted at a temperature of from 0 to 35° C. for a time of from 1 to 60 minutes and the hydrolysis product mixture is allowed to afterreact at a temperature of from 35 to 85° C. for from 10 minutes to 4 hours.
12. The storage stable composition as claimed in claim 1 , further comprising replacing the amount of alcohol removed by a corresponding amount of water.
13. A foundry mold or foundry core, comprising:
the storage stable composition claimed in claim 1 as a binder.
14. A method of coating a substrate surface, comprising:
coating the substrate surface with a composition which comprises the storage stable composition as claimed in claim 1 , to obtain a coated substrate.
15. The method as claimed in claim 14 , further comprising thermally curing the coated substrate.
16. The method as claimed in claim 14 , wherein said substrate surface comprises paper, paperboard, wood, chipboard, plastic, synthetic fibers, natural fibers, textile fibers, textiles, leather, glass fibers, rock wool, paint coats, masonry, ceramic, metal or metal alloys.
17. A coating obtained by applying the storage stable composition as claimed in claim 1 to a substrate surface and curing the applied coating.
18. An article, comprising a coating as claimed in claim 17 .
19. A curable coating agent, comprising the composition as claimed in claim 1 .
20. The storage stable composition as claimed in claim 1 , wherein component (iii) is acetic acid.