Method of separating nitrogen gas and molecular sieve carbon
View Patent ↗It is an object of the present invention to provide an industrially viable PSA process that requires small volumes of molecular sieve carbon and feed air. In order to achieve the above object, the PSA process uses the molecular sieve carbon satisfying the following relationships (I) and (II). (1)ln C ≦0.325+5.14×ln {(0.64+0.098)× Q /( P +0.098)} (I) (2)ln U ≦2.124−0.135×ln C (II) where C indicates an oxygen level (ppm) in the nitrogen gas product; Q indicates a volume of nitrogen gas produced per minute per unit effective volume of a single adsorption column; P indicates an adsorption pressure (MPa); and U indicates a ratio of the volume of the feed air to the volume of the nitrogen gas produced.
1. A process for separating nitrogen, wherein a feed gas made up mainly of nitrogen is fed under pressure to one of at least two adsorption columns packed with molecular sieve carbon to conduct high pressure adsorption, the one of at least two adsorption columns having completed high pressure adsorption is subjected to low pressure desorption, and the alternating cycle of the high pressure adsorption and the low pressure desorption are repeated in each adsorption column to separate nitrogen gas product, wherein
the molecular sieve carbon has 0.7 wt % or less ignition residue and the following relationships (I) and (II) are satisfied:
(1)ln C≦ 0.325+5.14×ln {(0.64+0.098)× Q /( P+ 0.098)} (I)
(2)ln U≦ 2.124−0.135×ln C (II)
where C indicates an oxygen level (ppm) in the nitrogen gas product; Q indicates a volume of nitrogen gas produced per minute per unit effective volume of a single adsorption column; P indicates an adsorption pressure (MPa); and U indicates a ratio of the volume of the feed air to the volume of the nitrogen gas produced.
2. The process for separating nitrogen according to claim 1 , wherein the molecular sieve carbon is made of a plant-based carbon material.
3. The process for separating nitrogen according to claim 2 , wherein the plant-based carbon material is coconut shell.
4. The process for separating nitrogen according to any one of claims 1 to 3 , wherein the molecular sieve carbon is spherical or cylindrical.
5. The process for separating nitrogen according to any one of claims 1 to 4 , wherein the molecular sieve carbon has an outer diameter of 0.4 to 1.5 mm.
6. A molecular sieve carbon with a ignition residue of 0.7% or less, wherein; when a feed gas made up mainly of nitrogen is fed under pressure to one of at least two adsorption columns packed with the molecular sieve carbon to conduct high pressure adsorption the one of at least two adsorption columns having completed high pressure adsorption is subjected to low pressure desorption and the alternating cycle of the high pressure adsorption and the low pressure desorption are repeated in each adsorption column to separate nitrogen gas; the molecular sieve carbon satisfies the following relationships (I′) and (II′)
(1)ln C≦ 0.325+5.14×ln {(0.64+0.098)× Q /( P+ 0.98)} (I′)
(2)ln U≦ 2.124−0.135×ln C (II′)
where C indicates an oxygen level (ppm) in the nitrogen gas product; Q indicates a volume of nitrogen gas produced per minute per unit effective volume of a single adsorption column; P indicates an adsorption pressure (MPa); and U indicates a ratio of the volume of the feed air to the volume of the nitrogen gas produced.
7. The molecular sieve carbon according to claim 6 , being made of a plant-based carbon material that is decalcified prior to pore adjustment.
8. The molecular sieve carbon according to claim 7 , wherein the plant-based carbon material is coconut shell.