Gas turbine engine components with aluminide coatings and method of forming such aluminide coatings on gas turbine engine components
View Patent ↗A turbine engine component ( 10 ) with a protective aluminide coating ( 14 ) that include additions of silicon and a dopant, such as yttrium and/or hafnium, in an amount effective to reduce sulfidation and a deposition process for forming such aluminide coatings ( 14 ). A silicon-containing layer ( 30 ) may be applied to the superalloy substrate ( 12 ) of the component ( 10 ) and the aluminide coating ( 14 ) formed by exposing component ( 10 ) and layer ( 30 ) to a vapor phase reactant containing the dopant. The aluminide coating ( 14 ), which contains dopant from the layer ( 30 ), may operate as a standalone environmental coating or as a bond coating for an optional ceramic thermal barrier layer ( 24 ). An optional zirconia layer ( 26 ) maybe provided between the aluminide coating ( 14 ) and the ceramic thermal barrier layer ( 24 ). Alternatively, the dopant may be included in the silicon-containing layer ( 30 ) applied to the component ( 10 ) before the aluminide coating ( 14 ) is formed and no vapor phase reactant containing the dopant is required.
1. A deposition process comprising:
obtaining a jet engine component of a nickel-based superalloy, the jet engine component having an external surface;
applying a liquid composition containing silicon and an additive that is dissolvable in the liquid composition and that supplies a dopant to at least a portion of the external surface; and
exposing the jet engine component to a donor material including a metal to form an aluminide coating including the metal from the donor material, silicon from the liquid composition, and the dopant from the liquid composition, the dopant being effective to reduce the transport of sulfur through the aluminide coating.
2. The deposition process of claim 1 further comprising:
forming a zirconia layer on the aluminide coating.
3. The deposition process of claim 2 further comprising:
forming a ceramic thermal barrier layer on the zirconia layer.
4. The deposition process of claim 2 wherein forming the zirconia layer further comprises:
depositing a zirconium layer on the aluminide coating; and
converting the zirconium layer to zirconia.
5. The deposition process of claim 4 wherein the zirconium layer is deposited in the same deposition environment in which the jet engine component is exposed to the donor material.
6. The deposition process of claim 4 wherein the zirconium layer is deposited at a deposition rate effective to provide surface texturing.
7. The deposition process of claim 6 further comprising:
forming a ceramic thermal barrier layer on the textured surface of the zirconia layer, the textured surface enhancing the adhesion of the ceramic thermal barrier layer to the jet engine component.
8. The deposition process of claim 1 wherein the dopant is selected from the group consisting of yttrium, hafnium, and combinations thereof.
9. The deposition process of claim 1 wherein the dopant is yttrium.
10. The deposition process of claim 1 wherein the dopant is hafnium.
11. The deposition process of claim 1 wherein the liquid composition containing silicon is a silane.