Method For Producing Negative Electrode For Lithium Secondary Battery
The lowness of the initial efficiency which is a drawback of lithium secondary batteries wherein a SiO negative electrode is used is largely made better without hindering a large initial charge capacity peculiar to the lithium secondary batteries. A fall in the cycle characteristic when the thickness of the SiO layer is made large is prevented. To realize these matters, a thin film of SiO is formed, as a negative electrode active material layer, on the surface of a current collector by vacuum evaporation or sputtering. The film is preferably formed by an ion plating process. The thickness of the SiO thin film is set to 5 μm or more. The surface roughness of the current collector is set to follows: the maximum height roughness Rz=5.0 or more. After the formation of the thin film, the film is thermally treated in a nonoxidative atmosphere.
1 . A process for producing a lithium secondary battery negative electrode, wherein a thin film of SiO is formed on the surface of a current collector, and subsequently the resultant is thermally treated in a nonoxidative atmosphere
2 . The process for producing a lithium secondary battery negative electrode according to claim 1 , wherein the temperature of the thermal treatment is from 650 to 850° C.
3 . The process for producing a lithium secondary battery negative electrode according to claim 1 , wherein the thickness of the SiO thin film is 5 μm or more.
4 . The process for producing a lithium secondary battery negative electrode according to claim 1 wherein the surface roughness of the current collector is as follows: Rz=5.0 or more.
5 . The process for producing a lithium secondary battery negative electrode according to claim 1 , wherein the SiO thin film is formed by vacuum evaporation or sputtering.
6 . The process for producing a lithium secondary battery negative electrode according to claim 5 , wherein the vacuum evaporation is an ion plating process.
7 . The process for producing a lithium secondary battery negative electrode according to claim 1 , wherein the SiO thin film is made of SiOx (0.5≦x≦1.2)after the thermal treatment.