Tantalum powder for the production of solid electrolyte capacitors
View Patent ↗A tantalum powder consisting of agglomerated primary particle with a minimum primary particle dimension of 0.2 to 0.8 μm, a specific surface area of 0.9 to 2.5 m 2 /g and a particle size distribution determined to ASTM B 822 corresponding to a D10 value of 5 to 25 μm, a D50 value of 20 to 140 μm and a D90 value of 40 to 250 μm, wherein the powder does not comprise an effective content of sintering protection agents.
1. A tantalum powder consisting of agglomerated primary particle with a minimum primary particle dimension of 0.2 to 0.8 μm, a specific surface area of 0.9 to 2.5 m 2 /g and a particle size distribution determined to ASTM B 822 corresponding to a D10 value of 5 to 25 μm, a D50 value of 20 to 140 μm and a D90 value of 40 to 250 μm, wherein the powder does not comprise and effective content of sintering protection agents.
2. A powder according to claim 1 , wherein the powder has a content of
P<30 ppm,
N<400 ppm,
B<10 ppm,
Si<20 ppm,
S<10 ppm, and
As<10 ppm.
3. A powder according to claim 2 , wherein the powder has a content of
P<10 ppm and
N<300 ppm.
4. A powder according to claim 3 , wherein the powder has a content of
N<100 ppm.
5. A tantalum powder according to 4 , which after pressing into a cylindrical shape with a diameter of 5.1 mm and a length of 5.1 mm and a compressed density of 5.0 g/cm 3 , exhibits a Chatillon compressive strength of greater than 5 kg.
6. A tantalum powder according to 1 , which after pressing into a cylindrical shape with a diameter of 5.1 mm and a length of 5.1 mm and a compressed density of 5.0 g/cm 3 , exhibits a Chatillon compressive strength of greater than 4 kg.
7. A tantalum powder according to 1 , which after pressing into a cylindrical shape with a diameter of 5.1 mm and a length of 5.1 mm and a compressed density of 5.0 g/cm 3 , exhibits a Chatillon compressive strength of greater than 5 kg.
8. A solid electrolyte capacitor anode of tantalum with a specific surface area active as a capacitor of 0.5 to 1 m 2 /g, which comprises substantially no sintering protection agents and wherein said anode having a specific capacitance of 40,000 to 150,000 μFV/g and a specific residual current of less than 1 nA/μ FV.
9. A solid electrolyte capacitor anode according to claim 8 , with a wire pull-out strength of greater than 30 kg.
10. A solid electrolyte capacitor anode according to claim 9 , with specific capacitance of 70,000 to 150,000 μFV/g and a specific residual current of less than 1 nA/μ FV.