Shear resistant printing ink vehicles
View Patent ↗The specification describes a process for making gelled ink resins which exhibit improved properties such as lower viscosity under low shear and less viscosity decrease with increasing shear. In a preferred embodiment, a rosin-based or hydrocarbon-based resin is mixed with an organic solvent and reacted with a polyamine reactant, such as melamine-formaldehyde resin or hexamethylene diamine, under conditions sufficient to produce a substantially covalently cross-link gelled resin. The resulting gelled resin resists viscosity breakdown under high shear conditions and may be used directly for making ink compositions, obviating the need for further gelation and avoiding the use of conventional organo-metallic gelling agents.
1. A process for making a high viscosity gelled ink resin composition which comprises mixing a rosin ester resin with an organic solvent and a crosslinking agent selected from the group consisting of melamine formaldehyde reactions products and urea formaldehyde reaction products to provide a reaction mass and heating the reaction mass under conditions sufficient to produce the gelled ink resin composition which exhibits increased viscosity as compared to the uncrosslinked resin solution and has improved stability against viscosity loss and elasticity degradation from mechanical and thermal stresses imposed during its use in high speed printing machines.
2. The process of claim 1 wherein the reaction is conducted under a nitrogen atmosphere.
3. The process of claim 1 wherein the rosin ester resin has an acid number of no more than about 25, and a solution viscosity in the range of from about Z5.0 to about Z7.0, as measured at 25° C. on one gram of resin dissolved in two grams of alkali refined linseed oil according to the Gardener Holt bubble tube test method.
4. The process of claim 1 wherein the rosin ester resin has an acid number of less than about 25, and a solution viscosity ranging from about Z5.5 to about Z8.0, as measured at 25° C. on one gram of resin dissolved in two grams of alkali refined linseed oil according to the Gardener Holt bubble tube test method.
5. The process of claim 1 wherein the crosslink agent is a melamine formaldehyde reaction product.
6. The process of claim 1 wherein the organic solvent is a high boiling organic solvent having a boiling point in the range of from about 220 to about 310° C.
7. The process of claim 1 wherein the crosslink agent is a urea formaldehyde reaction product.
8. The process of claim 1 wherein the rosin ester resin is selected from the group consisting of gum rosin resins, wood rosin resins, and tall oil rosin resins.
9. The process of claim 1 wherein the organic solvent includes a vegetable oil.
10. The process of claim 1 wherein the level of organic solvent is within the range of 0.7 to 1.5 parts by weight per part by weight of resin.
11. The process of claim 1 wherein the crosslinking agent is mixed into the reaction mass at a level which is within the range of 2 to 6 weight percent, based upon the total weight of resin and crosslinking agent.
12. The process of claim 1 wherein the reaction mass is heated to a temperature which is within the range of 120° C. to 220° C.
13. The process of claim 1 wherein the reaction mass is heated to a temperature which is within the range of 150° C. to 200° C.