Method for producing a work, jointing and surfacing compound for structural elements and its method of preparation
View Patent ↗The invention relates to a sealant compound comprising, in weight percent relative to the compound total volume: 40-60% of mineral filler whose diameter d50 ranges from 5 to 20 microns, 5-10% of hydrophobic expanded perlite whose diameter d50 ranges from 20 to 100 microns and 4-20% of binder. A method for preparing the inventive compound is also disclosed. Said invention also relates to producing a work provided with joints made of pointing and/or surfacing compound by applying said compound and/or pointing and surfacing by applying the compound which is characterised in that the compound is applied by airless process. According to the inventive method, said sealant compound is embodied such as described in the invention.
1. A method of producing a work, comprising juxtaposition of paper-faced plasterboards, optionally application of a tape, covering of the joint between the plasterboards by means of a drying compound applied by an airless technique, wherein the drying compound comprises, in percentages by weight relative to the total weight of the compound:
40 to 50% of a mineral filler having a diameter d 50 of between 10 and 15 microns;
5 to 10% of hydrophobic expanded perlite having a diameter d 50 of between 20 and 100 microns;
4 to 20% of a binder;
0.5 to 10% of a slip agent comprising a clay and/or talc and/or mica and/or a stearate;
1 to 15% of a water-retaining agent that is a cellulose derivative; and
1 to 15% of an antifoam agent,
wherein the compound has an apparent density of between 1 and 1.25, and a Brookfield viscosity of the compound on leaving a spray nozzle is between 0.2 and 0.6 times an original Brookfield viscosity value of the compound.
2. The method of claim 1 , the compound comprising:
40 to 50% of the mineral filler;
6 to 7.5% of the hydrophobic expanded perlite; and
5 to 10% of the binder.
3. The method of claim 1 , in which the hydrophobic expanded perlite has a d 50 of between 30 and 70 microns.
4. The method of claim 1 , in which the binder is chosen from polyvinyl alcohol homopolymers, polyvinyl acetate homopolymers (plasticized or unplasticized), ethylene/vinyl acetate copolymers (plasticized or unplasticized EVAs), ethylene/vinyl versatate copolymers, vinyl acetate/vinyl versatate copolymers, polyacrylics, vinyl acetate/acrylic copolymers, styrene/acrylic copolymers, styrene/butadiene copolymers, vinyl acetate/vinyl versatate/vinyl maleate terpolymers, vinyl acetate/vinyl versatate/acrylic terpolymers, acrylic terpolymers and blends thereof.
5. The method of claim 1 , in which the antifoam agent is a nonionic surfactant.
6. The method of claim 1 , wherein the compound further includes:
a silicone derivative, in an amount of 1 to 15%.
7. The method of claim 6 , in which the silicone derivative is a siliconate.
8. The method of claim 1 , wherein the compound comprises:
40 to 50% of calcium carbonate having a diameter d 50 of between 10 and 15 microns;
5 to 10% of hydrophobic expanded perlite having a diameter d 50 of between 30 and 70 microns;
5 to 10% of the binder;
1 to 5% of a slip agent comprising a clay and/or a stearate;
1 to 15% of the water-retaining agent;
1 to 15% of the antifoam agent; and optionally
1 to 15% of a silicone derivative.
9. The method of claim 1 , in which the density of the compound is between 0.9 and 1.3 kg/m 3 .
10. The method of claim 1 , in which the viscosity of the compound after resting for 24 hours may be between 150 000 cps and 1 500 000 cps.
11. The method of claim 1 , in which the viscosity under shear of the compound is equal to 0.2 to 0.6 times the viscosity without shear.
12. The method of claim 1 , in which the time for the yield point to recover has a characteristic time of between 1 and 120 min.
13. The method of claim 1 , the compound having a solids content of 50 to 70%.
14. The method of claim 1 , in which the constituents of the compound are mixed in any order.
15. The method of claim 1 , in which the perlite is mixed first and then the other components.
16. The method of claim 1 , in which part of the mineral filler is premixed with at least part of the components that are difficult to disperse.
17. The method of claim 1 , which includes a surfacing additional step by applying a second drying compound based on a filler and a binder, characterized in that the first and second compounds are applied by the airless technique.