View Patent ↗Disclosed herein are blowing agents comprising fluorocarbons and/or hydrofluorocarbons useful in foamable compositions. Also disclosed are methods for forming a foam comprising the aforementioned blowing agents.
1. A method of forming a polyisocyanate-based foam comprising
forming a blend by mixing a blowing agent comprising a hydrofluorocarbon, with
at least one polyol, wherein said blowing agent is not fully soluble in said polyol
reacting at least one organic polyisocyanate with said blend, wherein said blowing agent comprising a hydrofluorocarbon having the formula E- or Z—R1CH═CHR2, wherein R1 and R2 are, independently, C1 to C6 perfluoroalkyl groups.
2. The method of claim 1 , wherein said blend contains at least 5 to 50 wt. % blowing agent, based on the total weight of active hydrogen-containing compound and blowing agent.
3. The method of claim 2 , wherein said blend contains at least 5 to 25 wt. % blowing agent, based on the total weight of polyol and blowing agent.
4. A method of producing polyurethane foams, comprising the steps of blending at least one polyol and at least one blowing agent, to form B side mixture having the appearance of an emulsion, said blowing agent comprising a hydrofluorocarbons selected from the group consisting of E-CF3CH═CHCF3, Z—CF3CH═CHCF3, E-CF3CH═CHCF2CF3, and Z—CF3CH═CHCF2CF3, and reacting said B side mixture with an A side mixture, said A side mixture comprising at least one organic polyisocyanate.
5. The method of claim 4 , wherein the at least one organic polyisocyanate, the at least one polyol and the blowing agent of claim 1 are blended simultaneously.
6. The method of claim 5 , wherein the reacting step is performed in the presence of at least one catalyst.
7. The method of claim 5 , wherein the B side further comprises at least one auxiliary component, said auxiliary component selected from the group consisting of a surfactant, a flame retardant, a preservative, a colorant, an antioxidant, a reinforcing agent, a filler, an antistatic agent, or a combination thereof.
8. The method of claim 7 , wherein the at least auxiliary component is a surfactant present in a range of from about 0.2 to about 5 parts surfactant per 100 parts by weight polyol.
9. The method of claim 8 , wherein said surfactant is a liquid or solid organosilicone compound, a polyethylene glycol ether of a long chain alcohol, a tertiary amine or alkanolamine salt of a long chain alkyl acid sulfate ester, an alkyl sulfonic ester, or an alkyl arylsulfonic acid.
10. The method of claim 6 , wherein the at least one catalyst is present in a range of from about 0.1 to about 5 parts catalyst per 100 parts by weight of polyol.
11. The method of claim 1 wherein said at least one polyol is a polyester polyol.
12. The method of claim 11 wherein said at least on polyol is prepared by reacting a carboxylic acid with a polyhydric alcohol.
13. The method of claim 11 wherein said at least on polyol is prepared by reacting a carboxylic acid with a polyhydric alcohol.
14. The method of claim 1 , wherein the blowing agent is thoroughly mixed with the polyol.