Solution spun fiber process
View Patent ↗The invention relates to a process for forming fibers from a spinning solution utilizing a high speed rotary sprayer. The fibers can be collected into a uniform web for selective barrier end uses. Fibers with an average fiber diameter of less that 1,000 nm can be produced.
1. A fiber forming process comprising the steps of:
supplying a spinning solution having at least one polymer dissolved in at least one solvent to a rotary sprayer having a rotating conical nozzle, the nozzle having a curved concave inner surface and a forward surface discharge edge;
issuing the spinning solution from the rotary sprayer along the curved concave inner surface so as to distribute said spinning solution toward the forward surface of the discharge edge of the nozzle; and
forming separate fibrous streams which are thrown off the discharge edge by centrifugal force from the spinning solution while the solvent vaporizes to produce continuous polymeric fibers in the absence of an electrical field, wherein the fibers have an average fiber diameter of less than about 1,000 nm;
wherein the nozzle further comprises a distributor disk for directing the spinning solution towards the concave inner surface of the nozzle.
2. The process of claim 1 , wherein the polymer is selected from the group comprising polyalkylene oxides, poly(meth)acrylates, polystyrene based polymers and copolymers, vinyl polymers and copolymers, fluoropolymers, polyesters and copolyesters, polyurethanes, polyalkylenes, polyamides, polyaramids, thermoplastic polymers, liquid crystal polymers, engineering polymers, biodegradable polymers, bio-based polymers, natural polymers, and protein polymers.
3. The process of claim 1 , wherein the spinning solution has a concentration of polymer dissolved in solvent of about 1% by weight of polymer to about 90% by weight of polymer.
4. The process of claim 1 , wherein the spinning solution can be heated or cooled.
5. The process of claim 1 , wherein the spinning solution has a viscosity from about 10 cP to about 100,000 cP.
6. The process of claim 1 , wherein the spinning solution is supplied at a throughput rate from about 1 cc/min to about 500 cc/min.
7. The process of claim 1 , wherein the rotational speed of the nozzle is between about 10,000 rpm and about 100,000 rpm.
8. The process of claim 1 , wherein the average fiber diameter is about 100 nm to about 500 nm.
9. The process of claim 1 , further comprising flowing a shaping fluid around the nozzle to direct the spinning solution away from the rotary sprayer.
10. The process of claim 9 , wherein the shaping fluid comprises a gas.
11. The process of claim 10 , wherein the gas is air.
12. The process of claim 1 , further comprising collecting the fiber onto a collector to form a fibrous web.
13. The process of claim 12 , further comprising applying a vacuum through the collector to pull the fibers onto the collector to form a fibrous web