Polyethylene molding powder and porous articles made therefrom
View Patent ↗The present invention relates to a new molding powder comprising polyethylene polymer particles. The molecular weight of the polyethylene polymer is within the range of from about 600,000 g/mol to about 2,700,000 g/mol as determined by ASTM 4020. The average particle size of the particles of the polyethylene polymer is within the range of from about 5 microns to about 1000 microns and the polyethylene has a powder bulk density in the range of from about 0.10 to about 0.30 g/cc. Also disclosed is a process for molding a shape from a molding powder comprising the inventive polyethylene polymer particles, as well as porous articles made in accordance with the process. The articles have excellent porosity and good strength for porous and porous filtration applications.
1. A porous article prepared from a polyethylene powder, wherein the polyethylene powder comprises particles having porous particle morphology and porous surface features, a molecular weight within the range of from about 600,000 g/mol to about 1,800,000 g/mol as determined by ASTM 4020, an average particle size in the range of from about 5 microns to about 1000 microns, and a powder bulk density in the range of from about 0.10 to about 0.30 g/cc and the porous article has a porosity of between about 30% and about 85%, wherein the article has an average pore size of from about 50 μm to about 80 μm.
2. A process for forming a porous article comprising:
(a) providing a molding powder comprising polyethylene polymer particles having porous particle morphology and porous surface features, wherein the polyethylene polymer has a molecular weight within the range of from about 600,000 g/mol to about 1,800,000 g/mol as determined by ASTM 4020; the average particle size of the polyethylene polymer particles is within the range of from about 5 microns to about 1000 microns and the polymer particles have a powder bulk density in the range of from about 0.10 to about 0.30 g/cc;
(b) forming the molding powder into a desired shape;
(c) heating the shape to a temperature of 140° C. to 300° C. for a period of time sufficient to permit the polyethylene polymer to expand and soften, while maintaining a porosity of at least about 30% and optionally maintaining the shape under pressure; and
(d) thereafter cooling and recovering the porous article having a porosity of between about 30% and about 85%.
3. The process according to claim 2 , where the temperature is in the range of from about 150° C. and about 280° C.
4. The process according to claim 2 , where the temperature is in the range of from about 170° C. and about 260° C.
5. A process for forming a porous article comprising:
(a) providing a molding powder comprising polyethylene polymer particles having porous particle morphology and porous surface features, wherein the polyethylene polymer has a molecular weight within the range of from about 600,000 g/mol to about 1,800,000 g/mol as determined by ASTM 4020; the average particle size of the polyethylene polymer particles is within the range of from about 5 microns to about 1000 microns; and the polymer particles have a powder bulk density in the range of from about 0.10 to about 0.30 g/cc;
(b)forming the molding powder into a desired shape;
(c) heating the shape to a temperature of 140° C. to 300° C. for a period of time sufficient to permit the polyethylene polymer to expand and soften, while maintaining a porosity of at least about 30% and optionally maintaining the shape under pressure; and
(d)thereafter cooling and recovering the porous article having a porosity of from about 30% to about 85%.
6. A process for forming a porous article comprising:
(a) providing a molding powder comprising polyethylene polymer particles wherein the polyethylene polymer has a molecular weight within the range of from about 600,000 g/mol to about 1,800,000 g/mol as determined by ASTM 4020; the average particle size of the polyethylene polymer particles is within the range of from about 5 microns to about 1000 microns; and the polymer particles have a powder bulk density in the range of from about 0.10 to about 0.30 g/cc, and wherein the particles have porous surface features and porous powder morphology and the powder exhibits a characteristic flexural strength of at least about 0.7 MPa;
(b) forming the molding powder into a desired shape;
(c) heating the shape to a temperature of 140° C. to 300° C. for a period of time sufficient to permit the polyethylene polymer to expand and soften, while maintaining a porosity of at least about 30%, and optionally maintaining the shape under pressure; and
(d) thereafter cooling and recovering the porous article having a porosity of between about 30% and about 85%, wherein the article has an average pore size of from about 50 μm to about 80 μm.