Composite wire for wire-harness and process for producing the same
View Patent ↗A wire-harness use composite wire comprising a first element wire which comprises 0.01-0.25 mass % C, 0.01-0.25 mass % N, 0.5-4.0 mass % Mn, 16-20 mass % Cr,8.0-14.0 mass % Ni, and the balance of Fe and impurities and satisfies that a C+N content is in the range of 0.15 mass %≦C+N≦0.30 mass %, and a second element wire comprising at least one material selected from the group consisting of copper, copper alloy, aluminum, and aluminum alloy, the first element wire and the second element wire being twisted together.
1. A composite wire for wire-harness comprising a first element wire which comprises 0.01-0.25 mass % C, 0.01-0.25 mass % N, 0.5-4.0 mass % Mn, 16-20 mass % Cr, 8.0-14.0 mass % Ni, and the balance of Fe and impurities and satisfies that a C+N content is in the range of 0.15 mass %≦C+N≦0.30 mass %, and a second element wire comprising at least one material selected from the group consisting of copper, copper alloy, aluminum, and aluminum alloy, the first element wire and the second element wire being twisted together,
wherein the first element wire is drawn in a wire drawing process at a reduction in area of between 5% and 98%, to be adjusted to a predetermined diameter of wire and thereafter is heat-treated at a temperature of between 950° C. and 1,150° C. for a retention time of between 0.5 sec. and 60 sec. so that a tensile strength of the first element wire to be twisted together with the second element wire is in the range of between 800 N/mm 2 and less than 1,200 N/mm 2 .
2. The composite wire for wire-harness according to claim 1 , wherein the first element wire comprises not more than 10% by volume of a martensitic phase induced by a wiring process and the balance consisting of an austenite phase.
3. A production method of a composite wire for wire-harness comprising:
drawing a stainless steel wire which comprises 0.01-0.25 mass % C, 0.01-0.25 mass % N, 0.5-4.0 mass % Mn, 16-20 mass % Cr, 8.0-14.0 mass % Ni, and the balance of Fe and impurities and satisfies that a C+N content is in the range of 0.15 mass %≦C+N≦0.30 mass % at a reduction in area of between 5% and 98%, to be adjusted to a predetermined diameter of wire,
heat-treating the drawn wire at a temperature of between 950° C. and 1,150° C. for a retention time of between 0.5 sec. and 60 sec., and
twisting at least one stainless steel wire obtained together with at least one metal wire comprising at least one material selected from the group consisting of copper, copper alloy, aluminum, and aluminum alloy,
wherein a tensile strength of the stainless steel wire before twisted together is in the range of between 800 N/mm 2 and less than 1,200 N/mm 2 .