Cement compositions useful in oil and gas wells
View Patent ↗Cement compositions containing low reactivity materials are disclosed. The compositions are useful in conditions involving high temperatures, high pressures, and tectonic forces such as oil and gas wells. The cement compositions display increased compressive strength, flexural strength, and tensile strength. Fractures appear to occur in a non-linear fashion between the Interfacial Transition Zone (ITZ) of the particles, rather than in a straight line such as those observed in conventional cement materials.
1. A cement composition comprising cement and low reactivity particles,
wherein the low reactivity particles have a size of about 40 mesh to about 250 mesh, and
wherein the low reactivity particles are present at a concentration of about 30 weight percent to about 100 weight percent, based on the weight of the cement.
2. The composition of claim 1 , wherein the composition fractures in a non-linear manner when set.
3. The composition of claim 1 , wherein the cement is API Class A cement, API Class B cement, API Class C cement, API Class G cement, or API Class H cement.
4. The composition of claim 1 , wherein the cement is ASTM class I cement, ASTM class II cement, ASTM class III cement, ASTM class IV cement, or ASTM class V cement.
5. The composition of claim 1 , wherein the particles are silica sand.
6. The composition of claim 1 , wherein the particles are aluminum silicate, gilsonite, ground coal, adamantane, or fullerene.
7. The composition of claim 1 , further comprising water.
8. The composition of claim 7 , wherein the water is present at a concentration of about 30 weight percent to about 150 weight percent, based on the weight of the cement.
9. The composition of claim 1 , further comprising sand.
10. The composition of claim 1 , further comprising gravel.
11. The composition of claim 1 , further comprising a dispersant, a salt, a set retarder, a gas control agent, a free fluid control agent, a biopolymer, a weighting material, a fluid loss agent, a bonding agent, an extender, a reinforcing agent, or a gel.
12. The composition of claim 11 , wherein the weighting agent is hematite.
13. The composition of claim 11 , wherein the fluid loss agent is a hydroxyethylcellulose and AMPS copolymer.
14. The composition of claim 11 , wherein the bonding agent is polyvinyl alcohol.
15. The composition of claim 11 , wherein the extender is sodium montmorillonite, sodium metasilicate, or sodium silicate.
16. The composition of claim 11 , wherein the reinforcing agent is wollastonite, pyrophyllite, sepiolite, carbon whiskers, polypropylene whiskers, or nylon whiskers.
17. A cement composition comprising:
cement; and
silica sand having a size of about 40 mesh to about 250 mesh, and
wherein the silica sand is present at a concentration of about 30 weight percent to about 100 weight percent, based on the weight of the cement.
18. The composition of claim 17 , further comprising water.
19. The composition of claim 17 , further comprising water at a concentration of about 30 weight percent to about 150 weight percent, based on the weight of the cement.