Fiber reinforced cement composition and products and manufacturing process
This invention is a fiber reinforced cement composition comprising the following raw materials: a hydraulic inorganic material, a siliceous material, and a woody reinforcement wherein the siliceous material is a mixture of an average particle size of not less than 15 um and not more than 50 um which is burned ash of coal and/or rhyolite and an average particle size of not less than 1 um and not more than 15 um which is burned ash of coal and/or rhyolite.
1. A fiber reinforced cement composition comprising the following raw materials:
not less than 25% by mass and not more than 45% by mass of a hydraulic inorganic material;
not less than 50% by mass and not more than 65% by mass of a siliceous material;
not less than 5% by mass and not more than 12% by mass of a woody reinforcement;
not less than 1% by mass and not more than 7% by mass of mica; and
not less than 0.25% by mass and not more than 1.5% by mass of polyvinyl alcohol resin, wherein
the hydraulic inorganic material is a portland cement,
the siliceous material is a mixture of burned ash of coal and/or rhyolite having an average particle size of not less than 15 μm and not more than 50 μm and burned ash of coal and/or rhyolite having an average particle size of not less than 1 μm and not more than 15 μm, and
a woody reinforcement is needle-leaves-tree unbleached haft pulp and/or needle-leaves-tree bleached kraft pulp and used newspaper.
2. The fiber reinforced cement composition according to claim 1 , wherein burned ash of coal is fly ash and rhyolite is pearlstone.
3. The fiber reinforced cement composition according to claim 1 , wherein the woody reinforcement is a mixture of the needle-leaves-tree unbleached kraft pulp and/or the needle-leaves-tree bleached kraft pulp and the used newspaper in a ratio of the the needle-leaves-tree unbleached kraft pulp and/or the needle-leaves-tree bleached kraft pulp to the used newspaper in a range of from 1:1 to 4:1.
4. A fiber reinforced cement composition comprising the following raw materials:
not less than 25% by mass and not more than 45% by mass of the hydraulic inorganic material;
not less than 5% by mass and not more than 12% by mass of the woody reinforcement;
not less than 50% by mass and not more than 65% by mass of the siliceous material;
not less than 1% by mass and not more than 7% by mass of mica; and
not less than 0.25% by mass and not more than 1.5% by mass of polyvinyl alcohol resin, wherein
the hydraulic inorganic material is a portland cement,
the siliceous material comprises burned ash of coal and/or rhyolite having an average particle size of not less than 1 μm and not more than 15 μm and burned ash of coal and/or rhyolite having an average particle size of not less than 15 μm and not more than 50 μm, the amount of the burned ash of coal and/or the rhyolite having the average particle size of not less than 1 μm and not more than 15 μm being not less than 25% by mass and not more than 75% by mass of the whole siliceous material, and
a woody reinforcement is needle-leaves-tree unbleached kraft pulp and/or needle-leaves-tree bleached kraft pulp and used newspaper.
5. A fiber reinforced cement composition comprising the following raw materials:
not less than 25% by mass and not more than 45% by mass of the hydraulic inorganic material;
not less than 5% by mass and not more than 12% by mass of the woody reinforcement;
not less than 50% by mass and not more than 65% by mass of the siliceous material;
not less than 1% by mass and not more than 7% by mass of mica; and
not less than 0.25% by mass and not more than 1.5% by mass of polyvinyl alcohol resin, wherein
the hydraulic inorganic material is a portland cement,
the woody reinforcement is a mixture of needle-leaves-tree unbleached kraft pulp and/or the needle-leaves-tree bleached kraft pulp and used newspaper in a ratio of the needle-leaves-tree unbleached kraft pulp and/or the needle-leaves-tree bleached kraft pulp to the used newspaper in a range of from 1:1 to 4:1,
the siliceous material comprises fly ash and/or pearlstone having an average particle size of not less than 15 μm and not more than 50 μm and fly ash and/or pearlstone having an average particle size of not less than 1 μm and not more than 15 μm, the amount of the fly ash and/or the pearlstone having the average particle size of not less than 1 μm and not more than 15 μm being not less than 25% by mass and not more than 75% by mass of the whole siliceous material.
6. The fiber reinforced cement product manufactured from the fiber reinforced cement composition according to claim 4 .
7. The fiber reinforced cement product manufactured from the fiber reinforced cement composition according to claim 5 .
8. A process for manufacturing the fiber reinforced cement product comprising the steps of:
dispersing in water a fiber reinforced cement composition comprising the following raw materials:
not less than 25% by mass and not more than 45% by mass of a hydraulic inorganic material;
not less than 50% by mass and not more than 65% by mass of a siliceous material;
not less than 5% by mass and not more than 12% by mass of a woody reinforcement;
not less than 1% by mass and not more than 7% by mass of mica; and
not less than 0.25% by mass and not more than 1.5% by mass of polyvinyl alcohol resin, wherein
the hydraulic inorganic material is a portland cement,
the siliceous material is a mixture of burned ash of coal and/or rhyolite having an average particle size of not less than 15 μm and not more than 50 μm and burned ash of coal and/or rhyolite having an average particle size of not less than 1 μm and not more than 15 μm, and
a woody reinforcement is needle-leaves-tree unbleached kraft pulp and/or needle-leaves-tree bleached kraft pulp and used newspaper, so as to give a slurry of the raw materials;
forming a green mat from the slurry; and
pressing the green mat by press molding and thereafter curing the mat in an autoclave.
9. A process for manufacturing the fiber reinforced cement product comprising the steps of:
dispersing in water a fiber reinforced cement composition comprising the following raw materials:
not less than 25% by mass and not more than 45% by mass of the hydraulic inorganic material;
not less than 5% by mass and not more than 12% by mass of the woody reinforcement;
not less than 50% by mass and not more than 65% by mass of the siliceous material;
not less than 1% by mass and not more than 7% by mass of mica; and
not less than 0.25% by mass and not more than 1.5% by mass of polyvinyl alcohol resin, wherein
the hydraulic inorganic material is a portland cement,
the siliceous material comprises burned ash of coal and/or rhyolite having an average particle size of not less than 1 μm and not more than 15 μm and burned ash of coal and/or rhyolite having an average particle size of not less than 15 μm and not more than 50 μm, the amount of the burned ash of coal and/or the rhyolite having the average particle size of not less than 1 μm and not more than 15 μm being not less than 25% by mass and not more than 75% by mass of the whole siliceous material, and
a woody reinforcement is needle-leaves-tree unbleached kraft pulp and/or needle-leaves-tree bleached kraft pulp and used newspaper, so as to give a slurry of the raw materials;
forming a green mat from the slurry; and
pressing the green mat by press molding and thereafter curing the mat in an autoclave.
10. A process for manufacturing the fiber reinforced cement product comprising the steps of:
dispersing in water a fiber reinforced cement composition comprising the following raw materials:
not less than 25% by mass and not more than 45% by mass of the hydraulic inorganic material;
not less than 5% by mass and not more than 12% by mass of the woody reinforcement;
not less than 50% by mass and not more than 65% by mass of the siliceous material;
not less than 1% by mass and not more than 7% by mass of mica; and
not less than 0.25% by mass and not more than 1.5% by mass of polyvinyl alcohol resin, wherein
the hydraulic inorganic material is a portland cement,
the woody reinforcement is a mixture of needle-leaves-tree unbleached kraft pulp and/or the needle-leaves-tree bleached kraft pulp and used newspaper in a ratio of the needle-leaves-tree unbleached kraft pulp and/or the needle-leaves-tree bleached kraft pulp to the used newspaper in a range of from 1:1 to 4:1,
the siliceous material comprises fly ash and/or pearlstone having an average particle size of not less than 15 μm and not more than 50 μm and fly ash and/or pearlstone having an average particle size of not less than 1 μm and not more than 15 μm, the amount of the fly ash and/or the pearlstone having the average particle size of not less than 1 μm and not more than 15 μm being not less than 25% by mass and not more than 75% by mass of the whole siliceous material, so as to give a slurry of the raw materials;
forming a green mat from the slurry; and
pressing the green mat by press molding and thereafter curing the mat in an autoclave.