Modified surfaces for attachment of biological materials
The invention relates to bioactive surface coatings deposited on selected substrates. Surface nanostructured film coatings deposited on most metal or nonmetal substrates to provide surfaces can be engineered to promote enhanced tissue/cell adhesion. Attached cells, including osteoblasts, fibroblasts and endothelial cells, retain viability and will readily differentiate and proliferate under appropriate conditions. Fibroblasts and endothelial cells exhibit good attachment and growth on most coated substrates, except on nano surfaced structured silicone.
1 . A method for preparing a biocoated substrate, comprising:
depositing a metal ion plasma on a substrate to form a nano-structured surface of particles at a density of at least about 10 3 particles/cm 2 metal coating in a size range of about 1 to about 100 microns; and
contacting the deposited coating with one or more cells for a time sufficient to attach the one or more cells to the coating surface;
wherein the one or more cells attached to the deposited coating form a biocoated substrate that retains biological properties of said attached cells.
2 . The method of claim 1 wherein the one or more cells attached to the coated substrate are mononuclear cells.
3 . The method of claim 2 one or more cells is selected from the group consisting of endothelial, fibroblast, osteoblast, chondrocytes, muscle cells and mixtures thereof.
4 . The method of claim 1 wherein the depositing is by ion plasma deposition (IPD).
5 . The method of claim 4 wherein IPD deposited metals are nanoparticles between about 1 to about 100 nm size range.
6 . The method of claim 1 wherein the substrate is selected from the group consisting of UHMWPE, EPTFE, PTFE, PEEK, polypropylene, polyurethane, polyimide, polyester, nylon, titanium, steel, chromium, zirconium, nickel, nitinol, alloys and combinations thereof.
7 . The method of claim 4 wherein the ion plasma comprises nitinol, CoCrMo, gold, platinum, copper, tantalum, titanium, zirconium, hafnium, zinc or combinations thereof.
8 . The method of claim 7 wherein the ion plasma is nitinol, gold or titanium.
9 . The method of claim 1 wherein the substrate comprises a metal or polymer material device selected from the group consisting of catheters, valves, stents and implants.
10 . The method of claim 1 wherein the nano-structured surface has a nanoparticle density of about 10 3 particles/cm 2 to about 10 4 particles/cm 2 .
11 . The method of claim 1 wherein the deposited coating has a thickness of about 1 to about 3 microns.
12 . A composition comprising one or more bioviable cells attached to a nano-structured metal film characterized as ion plasma deposited metal particles up to about 1 micron in size distributed at a density of about 10 3 to 10 4 /cm 2 .
13 . The composition of claim 12 wherein the ion plasma deposited metal particles comprise Ag, Au, Ti, CoCrMo, or mixtures thereof.
14 . The composition of claim 12 wherein the bioviable cells are mononuclear cells.
15 . The composition of claim 14 wherein the mononuclear cells are fibroblasts, osteoblasts, chondrocytes, muscle, endothelial cells or mixtures thereof.
16 . The composition of claim 12 wherein the one or more cells are osteoblast cells attached to nanostructured titanium surface deposited on UHMWPE.
17 . The composition of claim 12 wherein the one or more cells are endothelial cells attached to nanostructured titanium deposited on UHMWPE or PTFE.
18 . A nanostructured metal surface coating on a substrate wherein the surface comprises particles up to 1 micron in size distributed on the substrate surface at a density of about 10 3 to about 10 4 /cm 2 and having a thickness of about 10 to about 100 micron.
19 . The nanostructured surface of claim 18 wherein the metal surface is gold, titanium or nitinol.
20 . A nanostructured surface coating that impregnates a metal or polymer substrate up to a depth of about 10 to about 100 nanometers wherein said coating is an ion plasma deposited metal comprised of nanoparticulates about 1 to about 5 nm, at a surface density of about 10 3 to 10 4 /cm 2 and a thickness of about 500 nm to about 100 microns.
21 . The nanostructured surface coating of claim 20 further comprising attached tissue cells.
22 . The nanostructured surface coating of claim 21 wherein the tissue cells are epithelial, fibroblast, chondrocytes, osteoblasts, muscle cells or mixtures thereof.
23 . The nanostructured surface coating of claim 20 wherein the ion plasma deposited metal coating is Au, Ag, Ti, CoCrMo or mixtures thereof.
24 . The nanostructured surface coating of claim 20 wherein the substrate is ultrahigh molecular weight polyethylene (UHMWPE), expanded poly tetrafluoroethylene (EPTFE), poly tetrafluoroethylene (PTFE), polyether ether ketone (PEEK), polypropylene, polyurethane, polyimide, polyester, nylon, titanium, steel, chromium, zirconium, nickel, nitinol, alloys and combinations thereof.
25 . The nanostructured surface coating of claim 20 wherein the substrate is steel, nitinol or aluminum oxide.
26 . The nanostructured surface coating of claim 20 wherein the ion plasma deposited metal is deposited from a controlled speed plasma arc target at a switching rate of about 300 Hz.
27 . The nanostructured surface coating of claim 20 wherein the coating comprises an implantable medical device.