Method and apparatus for evaluation and improvement of mechanical and thermal properties of CNT/CNF arrays
View Patent ↗A method and apparatus for the evaluation and improvement of the mechanical and thermal properties of carbon-nanotube (CNT) and carbon nanofiber (CNF) arrays grown on a substrate is disclosed. The Young's modulus of a CNT/CNF material is measured by applying an axial compressive force on the CNT/CNF array and measuring the applied forces and the induced displacements. Also disclosed are the evaluation of the nonlinear stress-strain relationship of the CNT/CNF material, increasing of the Young's modulus and decreasing the thermal resistance by application of a compressive load, the application of rapid thermal annealing to improve the quality of the CNT/CNF material and to reduce the interfacial thermal resistance, improvement of the bonding strength of the CNT/CNF array to a substrate, evaluation of the bonding strength of the CNT/CNF array to a substrate, evaluation of the shearing force at failure, and an analytical stress model that enables one to predict the interfacial shearing stress from the measured force.
1. A method for increasing thermal conductivity and thermal performance of material comprising an array of any of (i) carbon nanotubes (CNTs) arranged vertically, (ii) carbon nanofibers (CNFs) arranged vertically, and (iii) nanowires arranged vertically, comprising:
repeatedly applying a compressive force to said material, wherein the compressive force is applied in a direction parallel to the any of (i) carbon nanotubes (CNTs) arranged vertically, (ii) carbon nanofibers (CNFs) arranged vertically, and (iii) nanowires arranged vertically.
2. The method of claim 1 , wherein said compressive force is applied to said material at least four times.
3. The method of claim 1 , wherein said compressive force repetitively applied to said material until a resulting increase in thermal conductivity of said material is less than a predefined threshold.
4. The method of claim 1 , said array comprising individually separated, rod-like or tube-like nano-structures.
5. The method of claim 4 , wherein said individually separated, rod-like or tube-like nano-structures having a coverage density of between 15 and 40 percent.
6. The method of claim 4 , said individually separated, rod-like or tube-like nano-structures having a coverage density of between 25 and 40 percent.
7. A micro-cooler manufactured in accordance with the method of claim 1 .
8. A method of rapid thermal annealing (RTA) of a material of an array comprised of any of carbon nanotubes (CNTs), carbon nanofibers (CNFs), or nanowires, comprising:
placing said array at room temperature in an oxygen free environment;
annealing said array at a temperature higher than a growth temperature of said array; and
soaking said array in an oxygen free environment at said annealing temperature;
said RTA improving any of quality of said array material, reduction of interfacial thermal resistance, and bonding strength of said array material to a substrate.
9. The method of claim 8 , said step of placing said array in a chamber at room temperature in an oxygen free environment, further comprising:
pumping nitrogen gas and argon gas into said environment.
10. The method of claim 9 , further comprising:
placing said array in said environment for a period of about five minutes.
11. The method of claim 8 , said annealing including reaching a desired annealing temperature within thirty seconds.
12. The method of claim 11 , wherein said annealing temperature is within a range of 800 to 1050 degrees Celsius.
13. The method of claim 8 , said soaking said array in an oxygen free environment at said annealing temperature further comprising:
pumping gas nitrogen and argon gas into said environment.
14. The method of claim 13 , further comprising: placing said array in said environment for a period of one minute.
15. The method of claim 8 , said array comprising individually separated, rod-like or tube-like nano-structures.
16. The method of claim 15 , said individually separated, rod-like or tube-like nano-structures having a coverage density of between 15 and 40 percent.
17. The method of claim 15 , said individually separated, rod-like or tube-like nano-structures having a coverage density of between 25 and 40 percent.
18. A micro-cooler manufactured in accordance with the method of claim 8 .