Platinum-bismuth catalysts for treating engine exhaust
An engine exhaust catalyst containing precious metal nanoparticles is promoted with bismuth. The bismuth promotion improves the catalyst's CO oxidation performance. Also, by varying the amount of bismuth that is added, the NO conversion rate that can be realized with the catalyst can be controlled. The control over the NO conversion rate is important because the passive regenerative performance of a particulate filter used in engine exhaust systems is based on the amount NO 2 that is present in the exhaust stream that reaches the particulate filter. The amount of NO 2 being produced needs to be optimized (not necessarily maximized) so that adequate particulate filter regeneration performance can be maintained while avoiding unused, toxic NO 2 from being exhausted into the atmosphere.
1. An engine exhaust catalyst comprising an alumina carrier promoted with bismuth, the alumina carrier having a plurality of pores in which platinum metal particles are supported, wherein the platinum metal particles have been reduced in the pores of the alumina carrier.
2. The engine exhaust catalyst of claim 1 , wherein the platinum metal particles have been reduced in the pores of the alumina carrier by an in situ reduction process.
3. The engine exhaust catalyst of claim 2 , wherein the in situ reduction process comprises mixing an alumina carrier in powder form and a platinum salt in a solvent to create a mixture and adding a reducing agent into the mixture to cause the platinum metal particles to be reduced in the pores of the alumina carrier.
4. The engine exhaust catalyst of claim 1 , wherein the alumina carrier is promoted with bismuth after the platinum metal particles have been reduced in the pores of the alumina carrier.
5. The engine exhaust catalyst of claim 1 , wherein the alumina carrier comprises lanthanum-doped alumina.
6. A diesel engine exhaust catalyst comprising an alumina carrier promoted with bismuth, the alumina carrier having a plurality of pores, in which platinum metal particles are supported, wherein the amount of bismuth in the catalyst is about 0.1 weight percent to about 20 weight percent, and the amount of platinum in the catalyst is about 0.1 weight percent to about 10 weight percent.
7. The diesel engine exhaust catalyst of claim 6 , wherein the amount of bismuth in the catalyst is about 0.5 weight percent to about 8 weight percent, and the amount of platinum in the catalyst is about 1 weight percent to about 5 weight percent.
8. The diesel engine exhaust catalyst of claim 7 , wherein the bismuth is present in an amount of about 2 weight percent to about 4 weight percent and the platinum amount is about 3 weight percent.
9. The diesel engine exhaust catalyst of claim 8 , wherein the platinum metal particles have been reduced in the pores of the alumina carrier by an in situ reduction process comprising mixing an alumina carrier in powder form and a platinum salt in a solvent to create a mixture and adding a reducing agent into the mixture to cause the platinum metal particles to be reduced in the pores of the alumina carrier.
10. The diesel engine exhaust catalyst of claim 8 , wherein the platinum metal particles have been deposited in the pores of the alumina carrier by an impregnation process.
11. The diesel engine exhaust catalyst of claim 6 , wherein the alumina carrier is promoted with bismuth after the platinum metal particles have been deposited in the pores of the alumina carrier.