Woven or knitted fabric exhibiting reversibly changeable air permeability
View Patent ↗A multi-layer woven or knitted fabric exhibiting reversibly changeable air permeability, which contains reversibly crimping cellulose acetate fibers exhibiting a percentage of crimp of less than 10% at a humidity of 95% or above and a percentage of crimp of 20% or above at a humidity of 45% or below and which has a basis weight of 100 to 350 g/m 2 . When water content of the fabric is enhanced by the absorption of water or moisture, the air permeability of the fabric increases to inhibit in-clothes stuffiness or stickiness due to sweat and in-clothes temperature rise, while when the fabric has discharged the water into the outside environment, the air permeability of the fabric decreases to the original one to prevent the body temperature from lowering excessively because of the heat of vaporization and thus keep the in-clothes environment comfortable.
1. A woven or knitted fabric exhibiting reversibly changeable air permeability of a multilayer structure, wherein a front layer consists of a polyester fiber and a back layer consists of a mixed yarn of a polyester fiber and a cellulose acetate fiber having reversibly crimping property, and wherein the cellulose acetate fiber exhibits a percentage crimp of less than 10% at a humidity of not less than 95% and a percentage crimp of not less than 20% at a humidity of not more than 45%, and the woven or knitted fabric has a basis weight of 100 to 350 g/m 2 .
2. The woven and knitted fabric exhibiting reversibly changeable air permeability according to claim 1 , exhibiting not more than 50% of residual water content percentage 20 minutes after a start of measurement in the measurement of the residual water content percentage.
3. The woven or knitted fabric exhibiting reversibly changeable air permeability according to claim 1 , wherein a temperature rise after 10 minutes in measurement of an artificial skin temperature is not more than 4° C. under conditions of a heat supply amount 2.33 (w/100 cm 2 ) and a perspiration amount 0.5 (g/100 cm 2 ), and the artificial skin temperature drops to a temperature not more than an initial temperature within 5 minutes under conditions of a heat supply amount 0.58 (w/100 cm 2 ) and a perspiration amount 0 (g/100 cm 2 ).
4. The woven or knitted fabric exhibiting reversibly changeable air permeability according to claim 1 , wherein water absorption velocity measurement by a Larose method gives a value not less than 1 ml of an amount of water absorption 10 seconds after a start of the measurement.
5. The woven or knitted fabric exhibiting reversibly changeable air permeability according to claim 1 , wherein the front layer and the back layer have a different density.
6. The woven or knitted fabric exhibiting reversibly changeable air permeability according to claim 5 , wherein a ratio of the density of the front layer and the back layer is not less than 1.2.
7. The woven or knitted fabric exhibiting reversibly changeable air permeability according to claim 1 , wherein the multilayer structure comprises a middle layer in addition to the front layer and the back layer.