Hydrogenated nitrile rubber with narrow molecular weight distribution, a process for its preparation and a method of use
View Patent ↗A novel process produces a novel hydrogenated nitrile rubber (B) which features a very narrow molecular weight distribution and a correspondingly low value for the polydispersity index. The preparation process encompasses the treatment of a hydrogenated nitrile rubber (A) with ultrasound, whereupon the resultant hydrogenated nitrile rubber (B) has a lower weight-average molecular weight (M w ) than the hydrogenated nitrile rubber (A). The resultant hydrogenated nitrile rubber (B) has excellent suitability for the production of mouldings via processing by extrusion processes or by injection-moulding processes.
1. A process for preparation of a hydrogenated nitrile rubber (B), comprising exposing a solution, in a solvent of a hydrogenated nitrile rubber (A) to the effect of ultrasound, whereupon the resultant hydrogenated nitrile rubber (B) has lower weight-average molecular weight (M w ) than the hydrogenated nitrile rubber (A), and the resultant hydrogenated nitrile rubber (B) has a polydispersity D=M w M n which is less than or equal to 2.
2. The process according to claim 1 , wherein the hydrogenated nitrile rubber (A) used comprises a hydrogenated co- or terpolymer which contains repeating units of at least one conjugated diene, of at least one α,β-unsaturated nitrile and, optionally, of one or more copolymerizable monomers.
3. The process according to claim 1 or 2 , wherein the hydrogenated nitrile rubbers (A) have a weight-average molecular weight M w in the range from 200,000 to 1,000,000 and also a polydispersity D=M w /M n in the range from 1.9 to 8.
4. The process according to claim 1 or 2 , wherein the hydrogenated nitrile rubbers (A) have a weight-average molecular weight M w in the range from 200,000 to 400,000 and also a polydispersity D=M w /M n in the range from 2.2 to 5.
5. The process according to claim 1 or 2 , wherein the hydrogenated nitrile rubbers (A) have a weight-average molecular weight M w in the range from 200,000 to 300,000, and also a polydispersity D=M w /M n in the range from 2.5 to 4.
6. The process according to claim 1 or 2 , wherein ultrasound is used with a frequency of at least 18 kHz.
7. The process according to claim 1 or 2 , wherein ultrasound is used with a frequency in the range from 18 to 30 kHz.
8. The process according to claim 1 or 2 , wherein ultrasound is used with a frequency in the range from 19 to 25 kHz.
9. The process according to claim 1 or 2 , wherein the solvent used for the hydrogenated nitrile rubber (A) comprises dichloromethane, benzene, toluene, cyclohexane or monochlorobenzene.
10. The process according to claim 1 or 2 , which is carried out batchwise or continuously.
11. The process according to claim 1 or 2 , which is carried out at a temperature in the range from −30 to 100° C.