Synthetic rubber with narrow molecular weight distribution, a process for its preparation and a method of use
View Patent ↗A novel process is used to prepare synthetic rubbers (B) which feature very narrow molecular weight distribution and a correspondingly low value for the polydispersity index. The preparation process encompasses the treatment of a synthetic rubber with ultrasound, where the resultant synthetic rubber (B) has a lower weight-average molecular weight (M w ) than the synthetic rubber (A) used. The resultant synthetic rubbers (B) have excellent suitability for processing via extruder processes or injection-moulding processes.
1. A process for preparation of a synthetic rubber (B), comprising exposing a synthetic rubber (A) to the effect of ultrasound via immersion of a sonotrode into a solution, in a solvent, of the synthetic rubber (A), wherein the resultant synthetic rubber (B) has a lower weight-average molecular weight (M w ) than the synthetic rubber (A), and the polydispersity of the synthetic rubber (B) is less than or equal to 2,
wherein synthetic rubber (B) is selected from the group consisting of nitrite rubbers (NBR), hydrogenated nitrite rubbers (HNBR), ethylene-vinyl acetate copolymers EVM, EPDM rubbers, emulsion styrene-butadiene rubber (ESBR), chlorine rubbers (CR), polybutadiene rubbers (BR), acrylate rubbers (ACM), fluororubbers (FKM), IIR and halo IIR; and
synthetic rubber (A) is selected from the group consisting of nitrile rubbers (NBR), hydrogenated nitrite rubbers (HNBR), ethylene-vinyl acetate copolymers EVM, EPDM rubbers, emulsion styrene-butadiene rubber (ESBR), chlorine rubbers (CR), polybutadiene rubbers (BR), acrylate rubbers (ACM), fluororubbers (FKM), IIR and halo IIR.
2. The process according to claim 1 , wherein the synthetic rubbers (A) have a weight-average molecular weight M w in the range from 200,000 to 1,000,000 and also a polydispersity D=M w /M n , in the range from 2.2 to 5.
3. The process according to claim 1 , wherein the synthetic rubbers (A) have a weight-average molecular weight M w in the range from 200,000 to 400,000 and also a polydispersity D=M w /M n in the range from 2.2 to 5.
4. The process according to claim 1 , wherein the synthetic rubbers (A) have a weight-average molecular weight M w in the range from 200,000 to 300,000 and also a polydispersity D=M w /M n in the range from 2.5 to 4.
5. The process according to claim 1 , wherein ultrasound is used with a frequency of at least 18 kHz.
6. The process according to claim 1 , wherein ultrasound is used with a frequency in the range from 18 to 30 kHz.
7. The process according to claim 1 , wherein ultrasound is used with a frequency in the range from 19 to 25 kHz.
8. The process according to claim 1 , wherein the solvent used for the synthetic rubber (A) comprises dichloromethane, benzene, toluene, cyclohexane or monochlorobenzene.
9. The process according to claim 1 , which is carried out batchwise or continuously.
10. The process according to claim 1 , which is carried out at a temperature in the range from −30 to 100° C.