Transparent polymeric electrodes for electro-optical structures, processes for producing the same, and dispersions used in such processes
View Patent ↗The invention concerns a process for producing transparent multi-layer electrodes from conductive polymers, electrodes produced by this process and their use in electro-optical structures.
1. A dispersion comprising at least one polymeric anion, at least one solvent and at least one polythiophene having repeating units corresponding to the general formula (I):
wherein A in each repeating unit independently represents a substituted or unsubstituted C 1 to C 5 alkylene radical, each R independently represents a linear or branched, substituted or unsubstituted C 1 to C 18 alkyl radical, a substituted or unsubstituted C 5 to C 12 cycloalkyl radical, a substituted or unsubstituted C 6 to C 14 aryl radical, a substituted or unsubstituted C 7 to C 18 aralkyl radical, a substituted or unsubstituted C 1 to C 4 hydroxyalkyl radical or a hydroxyl radical, x in each repeating unit independently represents a whole number from 0 to 8,
wherein the at least one polymeric anion and the at least one polythiophene are present in a weight ratio of 1:1 to 5:1, wherein the dispersion has a viscosity of 5 to 300 mPas, and wherein 50 wt. % of particles in the dispersion are smaller than 50 nm, such that a film produced from the dispersion has an electrical conductivity of at least 300 S/cm and a surface roughness Ra of less than 2.5 nm.
2. The dispersion according to claim 1 , further comprising one or more additives selected from the group consisting of ether group-containing compounds, lactone group-containing compounds, amide group-containing compounds, lactam group-containing compounds, sulfones, sulfoxides, sugars, sugar derivatives, sugar alcohols, furan derivatives, dialcohols, polyalcohols and mixtures thereof, wherein the one or more additives is present in an amount of at least 0.1 wt. %, based on the dispersion.
3. A dispersion comprising at least one polymeric anion, at least one solvent and at least one polythiophene having repeating units corresponding to the general formula (I):
wherein A in each repeating unit independently represents a substituted or unsubstituted C 1 to C 5 alkylene radical, each R independently represents a linear or branched, substituted or unsubstituted C 1 to C 18 alkyl radical, a substituted or unsubstituted C 5 to C 12 cycloalkyl radical, a substituted or unsubstituted C 6 to C 14 aryl radical, a substituted or unsubstituted C 7 to C 18 aralkyl radical, a substituted or unsubstituted C 1 to C 4 hydroxyalkyl radical or a hydroxyl radical, x in each repeating unit independently represents a whole number from 0 to 8,
wherein the at least one polymeric anion and the at least one polythiophene are present in a weight ratio of 1:1 to 5:1, wherein the dispersion has a viscosity of 5 to 300 mPas, and wherein 50 wt. % of particles in the dispersion are smaller than 30 nm, such that a film produced from the dispersion has an electrical conductivity of at least 300 S/cm and a surface roughness Ra of less than 2.5 nm.
4. The dispersion according to claim 3 , further comprising one or more additives selected from the group consisting of ether group-containing compounds, lactone group-containing compounds, amide group-containing compounds, lactam group-containing compounds, sulfones, sulfoxides, sugars, sugar derivatives, sugar alcohols, furan derivatives, dialcohols, polyalcohols and mixtures thereof, wherein the one or more additives is present in an amount of at least 0.1 wt. %, based on the dispersion.