Hydrophilic coating and method of making same
View Patent ↗Methods of making hydrophilic coatings having anti-fog properties, and hydrophilic articles are provided. In certain example instances, a substrate supports a surfactant and polyethylenimine. The method includes forming a polyethylenimine-solvent mixture; applying a surfactant to a surface of the substrate; and applying the polyethylenimine-solvent mixture to the dried surfactant on the surface of the substrate. After drying or curing, the resulting coating may be hydrophilic thereby allowing water or the like to easily shed therefrom (e.g., providing anti-fog properties).
1. A method of making a coated article including a hydrophilic coating having hydrophilic properties, the method comprising:
dissolving at least polyethylenimine in at least water to form a polyethylenimine water mixture and mixing the polyethylenimine water mixture, wherein the polyethylenimine water mixture comprises less than or equal to 10 percent polyethylenimine by weight;
applying a surfactant to a surface of a substrate and drying to form a first layer, wherein the surfactant includes a nonionic surfactant and comprises a fluoroalkyl substituted polyethylene glycol;
applying the polyethylenimine water mixture over at least the first layer on the substrate and drying the polyethylenimine water mixture to form a second layer; and
wherein the second layer is hydrophilic, such that a sessile drop of water in contact with the second layer exhibits a contact angle of less than or equal to 25 degrees.
2. The method of claim 1 , wherein the polyethylenimine water mixture comprises less than or equal to 8 percent polyethylenimine by weight.
3. The method of claim 1 , wherein the polyethylenimine water mixture comprises less than or equal to 6 percent polyethylenimine by weight.
4. The method of claim 3 , wherein the polyethylenimine water mixture comprises less than or equal to 4 percent polyethylenimine by weight.
5. The method of claim 4 , wherein the polyethylenimine water mixture comprises less than or equal to 2 percent polyethylenimine by weight.
6. The method of claim 5 , wherein the polyethylenimine water mixture comprises less than or equal to 0.5% percent polyethylenimine by weight.
7. The method of claim 1 , wherein the contact angle is less than or equal to 20 degrees.
8. The method of claim 7 , wherein the contact angle is less than or equal to 15 degrees.
9. The method of claim 8 , wherein the contact angle is less than or equal to 10 degrees.
10. The method of claim 1 , wherein the substrate comprises a glass substrate.
11. The method of claim 1 , wherein the substrate comprises a plastic substrate.
12. The method of claim 11 , wherein the substrate comprises polyvinyl butyral.
13. The method of claim 1 , wherein the first layer and the second layer have a combined thickness of between 0.5 to 3 micrometers.
14. The method of claim 13 , wherein the combined thickness is between 1 and 2.5 micrometers.
15. The method of claim 14 , wherein the combined thickness is between 1.3 and 2.1 micrometers.
16. The method of claim 1 , wherein the coated article is a freezer door, and the coating is provided on an interior surface of the freezer door.
17. A method of making a coated article including forming a hydrophilic coating having anti fog properties on a substrate, the method comprising:
dissolving at least polyethylenimine in at least a solvent to form a polyethylenimine solvent mixture and optionally mixing the polyethylenimine solvent mixture;
applying a surfactant to a surface of a substrate and drying to form a first layer, wherein the surfactant includes a nonionic surfactant and comprises a fluoroalkyl substituted polyethylene glycol;
applying the polyethylenimine solvent mixture over at least the dried surfactant on the substrate, and drying the polyethylenimine water mixture to form a second layer, wherein the drying of the polyethylenimine water mixture occurs in ambient atmosphere; and
wherein the second layer is hydrophilic, such that a sessile drop of water in contact with the second layer exhibits a contact angle of less than or equal to 25 degrees.
18. The method of claim 17 , wherein the solvent comprises an alcohol.
19. The method of claim 18 , wherein the alcohol comprises one or more of isopropanol, methanol, and ethanol.
20. The method of claim 17 , wherein the polyethylenimine solvent mixture comprises less than or equal to 15 percent polyethylenimine by weight.
21. The method of claim 17 , wherein the substrate comprises glass or plastic.
22. The method of claim 17 , wherein a sessile drop of water in contact with the second layer exhibits a contact angle of less than or equal to 15 degrees.
23. The method of claim 17 , wherein the first layer and the second layer have a combined thickness of from about 0.5 to 3 micrometers.
24. The method of claim 17 , wherein the coated article is a freezer door, and the coating is provided on an interior surface of the freezer door.
25. A method of making a coated article including a hydrophilic coating having hydrophilic properties, the method comprising:
dissolving at least polyethylenimine in at least water to form a polyethylenimine water mixture and mixing the polyethylenimine water mixture;
applying a surfactant to a surface of a substrate and drying to form a first layer, wherein the surfactant is a nonionic surfactant and comprises a derivative of polyethylene glycol comprising fluoroalkyl substituted polyethylene glycol;
applying the polyethylenimine water mixture over at least the first layer on the substrate and drying the polyethylenimine water mixture to form a second layer; and
wherein the second layer is hydrophilic, such that a sessile drop of water in contact with the second layer exhibits a contact angle of less than or equal to 25 degrees.
26. The method of claim 25 , wherein the coated article comprises a freezer door, and the coating is provided on an interior surface of the freezer door.