Process for producing seamless steel pipe
View Patent ↗A process for producing a seamless steel pipe, in which the occurrence of inner surface flaws in the pipe can be reduced through the lowering of the friction coefficient during the elongation rolling by means of a mandrel mill is provided. The reduction of inner surface flaws is accomplished through the use of a lubricant composed mainly of either or both of graphite and mica coated to the surface of a mandrel bar, and another lubricant composed mainly of an alkali metal borate that is applied onto the inner surface of the hollow stock pipe. The temperature of the pipe prior to receiving the lubricant, during lubricant application, and prior to elongation rolling is controlled. The time between descaling or piercing and lubricant application and between lubricant application and elongation rolling is also controlled.
1. A process for producing a seamless steel pipe excellent in inner surface quality, characterized by, comprising, during the elongation rolling of a hollow stock pipe by means of a mandrel mill,
coating with a lubricant composed mainly of either or both of graphite and mica to the surface of a mandrel bar
and further applying a lubricant composed mainly of an alkali metal borate onto the inner surface of the hollow stock pipe,
and also characterized by satisfying the following requirements (a) to (d):
(a) the temperature of inner surface of stock pipe immediately after the completion of piercing being set for not lower than 1150° C., and the time from the completion of piercing to the initiation of applying the lubricant composed mainly of an alkali metal borate, or the time from the completion of descaling to the initiation of applying the lubricant composed mainly of an alkali metal borate is set for 5 to 60 seconds,
(b) the temperature of inner surface of stock pipe during applying the lubricant composed mainly of an alkali metal borate being set for not lower than 1100° C.,
(c) the time from the completion of applying the lubricant composed mainly of an alkali metal borate to the initiation of elongation rolling being set for not less than 10 seconds:
(d) the temperature of inner surface of stock pipe immediately before the elongation rolling being set within a range from 1000 to 1170° C.