Coated article having low-E coating with ion beam treated IR reflecting layer and corresponding method
View Patent ↗A coated article is provided that may be used as a vehicle windshield, insulating glass (IG) window unit, or the like. An ion beam is used during at least part of forming an infrared (IR) reflecting layer(s) of such a coated article. Advantageously, this has been found to improve sheet resistance (R s ) properties, solar control properties, and/or durability of the coated article. Other layers may also be ion beam treated in certain example embodiments.
1. A coated article including a glass substrate supporting a coating, wherein the coating comprises:
at least one dielectric layer;
an IR reflecting layer provided on the substrate over at least the dielectric layer;
another dielectric layer provided on the substrate over at least the IR reflecting layer and the at least one dielectric layer; and
wherein the IR reflecting layer comprises silver and has compressive stress, and wherein the IR reflecting layer is graded with respect to argon content so that an upper portion of the IR reflecting layer has a higher argon concentration than does a lower portion of the IR reflecting layer.
2. The coated article of claim 1 , wherein the IR reflecting layer is substantially free of oxygen in at least a portion thereof.
3. The coated article of claim 1 , wherein the IR reflecting layer is substantially metallic or metallic.
4. The coated article of claim 1 , wherein the upper portion of the IR reflecting layer has an argon concentration at least 10% higher than that of the lower portion of the IR reflecting layer.
5. The coated article of claim 4 , wherein the upper portion of the IR reflecting layer has an argon concentration at least 20% higher than that of the lower portion of the IR reflecting layer.
6. The coated article of claim 1 , wherein the at least one dielectric layer comprises silicon nitride.
7. The coated article of claim 1 , wherein the coated article has a visible transmission of at least 70% and a sheet resistance (Rs) of no greater than 5.0 ohms/square.
8. The coated article of claim 1 , further comprising a layer comprising zinc oxide, wherein the IR reflecting layer is located directly on and contacting the layer comprising zinc oxide.
9. The coated article of claim 1 , wherein the IR reflecting layer comprises Ag and/or Au.
10. The coated article of claim 1 , wherein the IR reflecting layer has compressive stress of from about 50 MPa to 2 GPa.
11. A coated article including a glass substrate supporting a coating, wherein the coating comprises:
at least one dielectric layer;
an IR reflecting layer provided on the substrate over at least the dielectric layer;
another dielectric layer provided on the substrate over at least the IR reflecting layer and the at least one dielectric layer; and
wherein the IR reflecting layer has different portions which differ with respect to content of an inert element, so that an upper portion of the IR reflecting layer has a higher concentration of the inert element than does a lower portion of the IR reflecting layer.
12. The coated article of claim 11 , wherein the inert element is argon.
13. The coated article of claim 11 , wherein the IR reflecting layer comprises silver and has compressive stress of from about 50 MPa to 2 GPa.
14. The coated article of claim 11 , wherein the IR reflecting layer is substantially free of oxygen in at least a central portion thereof.
15. The coated article of claim 11 , wherein the IR reflecting layer is substantially metallic or metallic.
16. The coated article of claim 11 , wherein the upper portion of the IR reflecting layer has an argon concentration at least 10% higher than that of the lower portion of the IR reflecting layer.
17. The coated article of claim 11 , wherein the upper portion of the IR reflecting layer has an argon concentration at least 20% higher than that of the lower portion of the IR reflecting layer.
18. The coated article of claim 11 , wherein the at least one dielectric layer comprises silicon nitride.
19. The coated article of claim 11 , wherein the coated article has a visible transmission of at least 70% and a sheet resistance (R s ) of no greater than 5.0 ohms/square.
20. The coated article of claim 11 , further comprising a layer comprising zinc oxide, wherein the IR reflecting layer is located directly on and contacting the layer comprising zinc oxide.
21. The coated article of claim 11 , wherein the IR reflecting layer comprises Ag and/or Au.