Microwell cell-culture device and fabrication method
View Patent ↗Methods for fabricating microfluidics devices, microfluidics cell-culture device and systems having a substrate, a microchannel through which liquid can be moved from one station to another within the device, the fabrication methods using semi-rigid materials during molding that are incorporated into the final device.
1. A method of molding an elastomeric part comprising:
(a) preparing a mold having a surface coating;
(b) dispensing an elastomer precursor over the coated mold;
(c) placing a semi-rigid sheet on top of the elastomer precursor such that a first side of the sheet is in contact with the elastomer precursor;
(d) at least partially curing the elastomer precursor;
(e) permanently joining the semi-rigid sheet to the elastomer precursor;
(f) removing the joined semi-rigid sheet and the at least partially cured elastomer from the mold;
(g) forming one or more access holes through the semi-rigid sheet and into the molded elastomer;
(h) bonding the surface of the elastomer opposite the semi-rigid sheet to a substrate; and
(g) attaching a second side of the semi-rigid sheet to a structure for accessing the molded elastomer.
2. The method of claim 1 , further comprising coating the first side of the semi-rigid sheet with an adhesion promoter prior to said placing.
3. The method of claim 2 , wherein said coating step is done by plasma treatment, chemical vapor deposition or glow discharge.
4. The method of claim 1 wherein said at least partially cured elastomer is less than 0.5 mm in height.
5. The method of claim 1 , further wherein the curing step and the permanently joining step are combined.
6. The method of claim 1 , further comprising:
wherein the molded elastomer comprises a plurality of microfluidic structures; and
wherein the attaching comprises bonding the semi-rigid sheet to a fluid reservoir plate structure with one or more fluid reservoirs thereby having a fluidic connection through the access holes to the plurality of microfluidic structures.
7. The method of claim 1 , further wherein:
the bonding comprises bonding the exposed surface of the elastomer to a rigid substrate to enclose channels and chambers imprinted in the elastomer by the mold as well as to seal off the access holes.
8. The method of claim 1 , further wherein the substrate is of a material selected from the group consisting of: glass, metal oxides, silicon with an oxide surface, or other suitable materials.
9. The method of claim 1 , further comprising
joining the molded surface of the at least partially cured elastomer to a second at least partially cured elastomer, prior to forming the one or more access holes.
10. The method of claim 9 further wherein the second at least partially cured elastomer is removed from a mold after the joining.
11. The method of claim 9 further comprising fully curing the multilayer elastomer.
12. The method of claim 1 further comprising:
the semi-rigid sheet comprises an adhesive primer applied to a sheet of transparent plastic; and
the elastomer precursor comprises uncured PDMS.
13. The method of claim 1 further wherein the mold is a silicon mold containing micro-features.
14. The method of claim 12 further comprising:
the at least partially curing comprises curing the PDMS in contact with the primed plastic and the mold to form a permanently bonded plastic/PDMS module from the mold; and
the bonding comprises gluing the plastic/PDMS module to a reservoir structure.
15. The method of claim 1 , further wherein the semi-rigid sheet is chosen from the group consisting of:
an acrylic polymer,
polymethyl methacrylate (PMMA),
polycarbonate,
polystyrene,
polynorbornene,
polyethylene terephthalate,
polyethylene,
polypropylene and
poly(4-methyl-1-pentene).
16. The method of claim 1 , wherein the semi-rigid sheet is at least about 1.5 mm thick.
17. The method of claim 1 , further wherein:
the placing comprises laying the semi-rigid sheet on top of the elastomer such that gravity and surface tension work to bring the sheet flat against the entire surface of the elastomer.
18. The method of claim 1 , further wherein:
the placing comprises laying the semi-rigid sheet on top of the elastomer wherein the mold and elastomer are situated within a fixed height spacer fixture with the sheet positioned over the edges of the spacer to ensure that the sheet lies parallel to the molded surface.
19. The method of claim 1 , further comprising:
situating the mold within a fixed height spacer;
dispensing a fixed volume of the elastomer precursor sufficient to form a desired thickness of said elastomer onto the mold; and
placing the semi-rigid sheet on top of the spacer fixture such that the sheet contacts and spreads the elastomer out over the entire mold surface.
20. The method of claim 19 further wherein the desired thickness is greater than about 200 μm thick; and the semi-rigid sheet is greater than about 1.5 mm thick.
21. The method of claim 1 further comprising:
forming the access holes by piercing, drilling, ablating, or laser cutting.
22. The method of claim 1 further comprising:
forming the access holes by such that the location of the access holes correspond to inlet or outlet areas of microfluidic structures in the elastomer.