Container closure with a multi-layer oxygen barrier liner
A container closure with a multiple layer liner. The liner comprises a nylon gas transmission barrier and a non-nylon layer bonded by an adhesive layer. The nylon gas transmission barrier may contain an additional passive gas transmission component comprising an in-situ polymerized inorganic clay. An additional active gas transmission component comprising a chemically reactive scavenger may be incorporated into at least one layer of the multiple layer liner. Materials of the liner are selected for their process conditions and resulting resistance to degradation.
1 . (canceled)
2 . (canceled)
3 . (canceled)
4 . (canceled)
5 . (canceled)
6 . (canceled)
7 . (canceled)
8 . (canceled)
9 . (canceled)
10 . (canceled)
11 . (canceled)
12 . (canceled)
13 . (canceled)
14 . (canceled)
15 . (canceled)
16 . (canceled)
17 . A process for manufacturing a container closure liner, the process comprising the steps of:
selecting a nylon barrier material having a range of processing temperature parameters;
selecting a material based on ethylene vinyl acetate having processing temperature parameters in a range overlapping, or adjacent to, the nylon barrier materials processing temperature parameters;
selecting a tie material having processing temperature parameters in a range overlapping the processing temperature parameters of the nylon barrier material and the material based on ethylene vinyl acetate; and
co-extruding the nylon barrier material, the tie material and the material based on ethylene vinyl acetate.
18 . (canceled)
19 . (canceled)
20 . (canceled)
21 . A method of manufacturing a liner material, the method comprising:
(a) providing a nylon barrier layer material having an extrusion processing temperature range;
(b) providing one or more skin layer materials selected separately for each occurrence from EVA, EVA copolymers, and blends of each with polyolefin polymers wherein each said skin layer material optionally contains an active oxygen scavenging material, and wherein the processing temperature range of each of said skin layer material overlaps with or is adjacent to said nylon barrier material processing temperature range;
(c) providing one or more tie layer compositions compatible with said nylon barrier layer material and said skin layer material(s) wherein each said tie layer composition has a processing temperature range overlapping with the processing temperature ranges of said nylon barrier material and with at least one said skin layer material; and
(d) co-extruding materials provided in steps “a” to “c” to provide a multi-layered composite material having a nylon barrier layer, adhered to each of a first and second face thereof a layer comprising at least one tie layer composition, and adhered to a face of each tie layer material distal to said barrier layer, a layer of skin layer material compatible with said tie layer.
22 . The method of claim 21 , wherein the liner material is further characterized as having a peel test rating between each said polymer layer and said nylon layer of at least 8 lbs. force/inch as measured by ASTM method D 1876-2001.