Corrosion resistant thermal barrier coating material
View Patent ↗According to one exemplary embodiment, a method for forming a corrosion resistant thermal barrier coating material includes steps of blending indium oxide with at least one hydrate forming oxide to form a mechanical mixture, heating the mechanical mixture to a sufficiently high temperature to form an indate precursor, and blending the indate precursor with at least one non-hydrate forming oxide to form a co-stabilized mixture. In one embodiment, the co-stabilized mixture can be changed into an APS powder by using a powder forming method. In another embodiment, the co-stabilized mixture can be formed into a desired shape and heated to form an EB-PVD ingot.
1. A method for forming a corrosion resistant thermal barrier coating material, said method comprising steps of:
blending indium oxide with at least one indate forming oxide to form a mechanical mixture;
heating said mechanical mixture to form an indate precursor; and
blending said indate precursor with an oxide selected from the group consisting of zirconia and hafnia and blends thereof to form a co-stabilized mixture for use in producing said corrosion resistant thermal barrier coating material.
2. The method of claim 1 further comprising a step of using a powder forming method to change said co-stabilized mixture into an un-fired precursor powder.
3. The method of claim 2 further comprising a step of heating said un-fired precursor powder to form an APS powder.
4. The method of claim 2 further comprising a step forming said un-fired precursor powder into an ingot of a desired shape.
5. The method of claim 2 further comprising a step forming said un-fired precursor powder into an ingot of a desired shape and heating said ingot to form an EB-PVD ingot.
6. The method of claim 1 , wherein said at least one indate forming oxide is selected from the group consisting of lanthanum oxide, cerium oxide, praseodymium oxide, neodymium oxide, promethium oxide, samarium oxide, europium oxide, gadolinium oxide, terbium oxide, dysprosium oxide, holmium oxide, erbium oxide, thulium oxide, ytterbium oxide, lutetium oxide, magnesium oxide, calcium oxide, and yttrium oxide.
7. The method of claim 1 , wherein a chemical composition of said co-stabilized mixture is Zr 1-x-y In x M y O z .
8. The method of claim 7 , wherein M is selected from the group consisting of calcia, magnesia, yttria, lanthanum oxide, cerium oxide, praseodymium oxide, neodymium oxide, promethium oxide, samarium oxide, europium oxide, gadolinium oxide, terbium oxide, dysprosium oxide, holmium oxide, erbium oxide, thulium oxide, ytterbium oxide, and lutetium oxide.
9. The method of claim 7 , wherein x has a value between approximately 0.01 and approximately 0.20.
10. The method of claim 7 , wherein y has a value between approximately 0.01 and 0.20.
11. The method of claim 7 , wherein z has a value between approximately 1.6 and 2.4.
12. The method of claim 1 , wherein said mechanical mixture is heated to a temperature between approximately 1150° C. and approximately 1400° C.
13. The method of claim 3 , wherein said un-fired precursor powder is heated to a temperature between approximately 1150° C. and approximately 1650° C.
14. The method of claim 5 , wherein said EB-PVD ingot is heated to a temperature between approximately 1150° C. and approximately 1650° C.
15. A method for forming a corrosion resistant thermal barrier coating material, said method comprising steps of:
forming an indate precursor from indium oxide and an indate forming oxide to recite an active, positive step and settle issues of indefiniteness; and
blending said indate precursor and an oxide selected from the group consisting of zirconia, hafnia, and a blend of zirconia and hafnia to form a mixture for use in producing said corrosion resistant thermal barrier coating material.
16. The method of claim 15 further comprising steps of:
forming an un-fired precursor powder from said mixture; and
heating said un-fired precursor powder to form an APS powder.
17. The method of claim 15 further comprising steps of:
forming an un-fired precursor powder from said mixture;
forming said un-fired precursor powder into an ingot of a desired shape; and
heating said ingot to form an EB-PVD ingot.
18. The method of claim 15 , wherein said indate forming oxide is selected from the group consisting of lanthanum oxide, cerium oxide, praseodymium oxide, neodymium oxide, promethium oxide, samarium oxide, europium oxide, gadolinium oxide, terbium oxide, dysprosium oxide, holmium oxide, erbium oxide, thulium oxide, ytterbium oxide, lutetium oxide, magnesium oxide, calcium oxide, and yttrium oxide.