An aqueous resin composition obtained by dissolving 100 parts by mass of acid-modified polyolefin and 5 to 60 parts by mass of surfactant in 15 to 1900 parts by mass of polymerizable monomer, adding water in the presence of basic compound to perform phase inversion emulsification, and polymerizing the monomer; an aqueous resin composition obtained by dissolving 100 parts by mass of acid-modified polyolefin and 5 to 60 parts by mass of surfactant in a first polymerizable monomer, adding water in the presence of basic compound to perform phase inversion emulsification, polymerizing the first monomer to form a resin composition, adding and polymerizing a second polymerizable monomer to the resin composition; the monomers being used in a total amount of 15 to 1900 parts by mass per 100 parts by mass of the acid-modified polyolefin; and paints, inks, adhesives, sealants and primers containing such composition as an active ingredient.
1. An aqueous resin composition obtained by dissolving 100 parts by mass of acid-modified polyolefin and 5 to 60 parts by mass of surfactant in 15 to 1900 parts by mass of polymerizable monomer, adding water in the presence of basic compound to perform phase inversion emulsification, and then polymerizing the polymerizable monomer wherein the resin has a mean particle diameter of not more than 0.5 μm.
2. The aqueous resin composition according to claim 1 , wherein the acid-modified polyolefin has a weight average molecular weight of 3000 to 200000 as measured by high temperature GPC.
3. The aqueous resin composition according to claim 1 , wherein the acid-modified polyolefin is obtained by graft-copolymerizing with a polyolefin 0.4 to 10 mass % of at least one member selected from unsaturated carboxylic acids and anhydrides thereof.
4. A process for producing an aqueous resin composition, the process comprising dissolving 100 parts by mass of acid-modified polyolefin and 5 to 60 parts by mass of surfactant in 15 to 1900 parts by mass of polymerizable monomer, adding water in the presence of basic compound to perform phase inversion emulsification, and then polymerizing the polymerizable monomer.
5. A paint for polyolefin films, sheets or molded articles, the paint comprising the aqueous resin composition according to claim 1 as an active ingredient.
6. An ink for polyolefin films, sheets or molded articles, the ink comprising the aqueous resin composition according to claim 1 as an active ingredient.
7. An adhesive for polyolefin films, sheets or molded articles, the adhesive comprising the aqueous resin composition according to claim 1 as an active ingredient.
8. A sealant for polyolefin films, sheets or molded articles, the sealant comprising the aqueous resin composition according to claim 1 as an active ingredient.
9. A primer for polyolefin substrates, the primer comprising the aqueous resin composition according to claim 1 as an active ingredient.
10. An aqueous resin composition obtained by dissolving 100 parts by mass of acid-modified polyolefin and 5 to 60 parts by mass of surfactant in a first polymerizable monomer, adding water in the presence of basic compound to perform phase inversion emulsification, polymerizing the first polymerizable monomer to form a resin composition, adding a second polymerizable monomer to the resin composition, and then polymerizing the second polymerizable monomer;
the first and second polymerizable monomers being used in a total amount of 15 to 1900 parts by mass per 100 parts by mass of the acid-modified polyolefin wherein the resin has a mean particle diameter of not more than 0.5 μm.
11. The aqueous resin composition according to claim 10 , wherein the acid-modified polyolefin has a weight average molecular weight of 3000 to 200000 as measured by high temperature GPC.
12. The aqueous resin composition according to claim 10 , wherein the acid-modified polyolefin is obtained by graft-copolymerizing with a polyolefin 0.4 to 10 mass % of at least one member selected from unsaturated carboxylic acids and anhydrides thereof.
13. A process for producing an aqueous resin composition, the process comprising the steps of dissolving 100 parts by mass of acid-modified polyolefin and 5 to 60 parts by mass of surfactant in a first polymerizable monomer, adding water in the presence of basic compound to perform phase inversion emulsification, polymerizing the first polymerizable monomer to form a resin composition, adding a second polymerizable monomer to the resin composition, and polymerizing the second polymerizable monomer;
the first and second polymerizable monomers being used in a total amount of 15 to 1900 parts by mass per 100 parts by mass of the acid-modified polyolefin.
14. A paint for polyolefin films, sheets or molded articles, the paint comprising the aqueous resin composition according to claim 10 as an active ingredient.
15. An ink for polyolefin films, sheets or molded articles, the ink comprising the aqueous resin composition according to claim 10 as an active ingredient.
16. An adhesive for polyolefin films, sheets or molded articles, the adhesive comprising the aqueous resin composition according to claim 10 as an active ingredient.
17. A sealant for polyolefin films, sheets or molded articles, the sealant comprising the aqueous resin composition according to claim 10 as an active ingredient.
18. A primer for polyolefin substrates, the primer comprising the aqueous resin composition according to claim 10 as an active ingredient.