Curable liquid resin optical fiber upjacket composition
View Patent ↗The present invention provides a curable liquid resin composition which, when cured, exhibits excellent removability from an adjacent coating layer and is suitable for an optical fiber upjacket material. The curable liquid resin optical fiber upjacket composition comprising a urethane (meth)acrylate or a (meth)acrylate oligomer, a reactive diluent, a polymerization initiator, and a polyol compound having a molecular weight of 1500 or more.
1. A curable liquid resin optical fiber upjacket composition, comprising:
(A) 30 to 90 wt % of a urethane (meth)acrylate,
(B) 1 to 70 wt % of a reactive diluent,
(C) 0.1 to 10 wt % of a polymerization initiator, and
(D) 0.1 to 50 wt % of a polyol compound having a molecular weight of 1500 or more, with the total amount of the components (A), (B), and (C) being 100 wt %.
2. A curable liquid resin optical fiber upjacket composition, comprising:
(A) 30 to 90 wt % of a (meth)acrylate oligomer,
(B) 1 to 70 wt % of a reactive diluent,
(C) 0.1 to 10 wt % of a polymerization initiator, and
(D) 0.1 to 50 wt % of a polyol compound having a molecular weight of 1500 or more, with the total amount of the components (A), (B), and (C) being 100 wt %.
3. The composition according to claim 1 , wherein the component (D) is a poly ether polyol.
4. The composition according to claim 1 , wherein the component (D) includes a polyol having a molecular weight of 1500 or more, the polyol having a branched structure in which a hydroxyl group is bonded to each branched chain terminal, with the value obtained by dividing the molecular weight of the polyol by the number of the hydroxyl groups bonded to the branched chain terminals being 500 to 2000.
5. The composition according to claim 1 , further comprising a silicone compound.
6. The composition according to claim 1 , wherein said silicone compound is a reactive silicone.
7. The composition according to claim 1 , further comprising a flame retardant.
8. The composition according to claim 1 , wherein said composition, when cured, has a Young modulus of about 100 MPa to about 600 MPa.
9. The composition according to claim 1 , wherein said composition, when cured, has a coating removal stress immediately after production of no more than 3.1 N, when measured by the 50 m/min test method.
10. The composition according to claim 9 , wherein said composition, when cured, has a coating removal stress after high-temperature and high-humidity test of no more than 3.1 N, when measured by the 50 m/min test method.
11. The composition according to claim 1 , wherein said composition, when cured, has a coating removal stress after production of less than 1800 g, when measured by the 20 inches/min test method.
12. The composition according to claim 9 , wherein said composition, when cured, has a coating removal stress immediately after high-temperature and high-humidity test of less than 1800 g, when measured by the 20 inches/min test method.
13. An optical fiber upjacket layer, comprising a cured product of the composition according to claim 1 .
14. An upjacketed optical fiber, comprising the optical fiber upjacket layer according to claim 13 .
15. A process of making an optical fiber upjacket layer comprising the step of curing the composition according to claim 1 .
16. An upjacket coating exhibiting good removability which comprises the optical fiber upjacket layer according to claim 13 .