View Patent ↗Agglomerated hollow particle latex is employed as a filler in the wet end of the paper-making process to provide paper with improved properties.
1. In a process for making a paper material, the process comprising forming an aqueous slurry comprising a filler and a predominantly cellulosic fiber pulp, forming a wet sheet from the slurry, and drying the sheet, the improvement comprising using as at least a portion of the filler an agglomerated hollow particle latex wherein at least about 30 weight percent of the solids of the latex are agglomerates, and wherein from 0.5 to about 50 weight parts of agglomerated hollow particle latex filler are used per 100 weight parts fiber, and wherein the agglomerated hollow particles are prepared from hollow latex particles with an interior void in the range of 10-70 percent of the volume of the latex particle.
2. The process of claim 1 wherein the agglomerated hollow particles have an average particle size of from about 3 to about 100 microns.
3. The process of claim 1 wherein the agglomerated hollow particles have a cationic surface charge.
4. The process of claim 1 wherein the agglomerated hollow particles have an anionic surface charge.
5. The process of claim 1 wherein the agglomerated hollow particles have a neutral surface charge.
6. The process of claim 1 wherein the agglomerated hollow particles are at least 50 weight percent of the total filler employed.
7. The process of claim 1 wherein the agglomerated hollow particles have a total void volume in the range of 30-90 percent.
8. A paper material prepared by the process of claim 1 .
9. A composition comprising an agglomerated hollow particle latex, wherein at least about 30 weight percent of the solids of the latex are agglomerates, wherein the agglomerated hollow particles have an average particle size of from about 3 to about 100 microns, and wherein the agglomerated hollow particles are prepared from hollow latex particles with an interior void in the range of 10-70 percent of the volume of the latex particle.
10. The composition of claim 9 wherein the agglomerated hollow particles have a cationic surface charge.
11. The composition of claim 9 wherein the agglomerated hollow particles have an anionic surface charge.
12. The composition of claim 9 wherein the agglomerated hollow particles have a neutral surface charge.
13. The composition of claim 9 wherein the agglomerated hollow particles have a total void volume in the range of 30-90 percent.
14. The composition of claim 9 wherein the agglomerated hollow particles have an average particle size of from about 5 to about 80 microns.
15. The composition of claim 9 wherein at least about 75 weight percent of the solids are agglomerates.