Catalyst carrier substrate coated with washcoat comprising fibrous material
View Patent ↗A solid catalyst carrier substrate coated with a surface area-enhancing washcoat composition including a catalytic component, a metal oxide and a refractory fibrous or whisker-like material having an aspect ratio of length to thickness in excess of 5:1.
1. A solid catalyst carrier substrate coated with a surface area-enhancing washcoat coating, which coating comprising a catalytic component, a metal oxide and a refractory fibrous or whisker-like material having an aspect ratio of length to thickness in excess of 5:1, wherein said substrate is coated with said washcoat coating and said washcoat coating has a thickness of from 5 to 100 μm.
2. A substrate according to claim 1 , wherein the aspect ratio of length to thickness is in excess of 50:1.
3. A substrate according to claim 1 , wherein the catalytic component comprises at least one metal.
4. A substrate according to claim 3 , wherein the at least one metal is selected from the group consisting of a precious metal, magnesium, nickel, cobalt, iron, vanadium, copper, molybdenum, aluminum, silicon and mixtures of any two or more thereof.
5. A substrate according to claim 4 , wherein the washcoat coating is formed by applying a washcoat composition to the substrate and drying the washcoat composition, and the metal is present at up to 30 wt % based on the total weight of the washcoat composition.
6. A substrate according to claim 3 , wherein the washcoat coating is formed by applying a washcoat composition to the substrate and drying the washcoat composition, and the metal is present at up to 30 wt % based on the total weight of the washcoat composition.
7. A substrate according to claim 1 , wherein the washcoat coating is chemically reactive.
8. A substrate according to claim 1 , wherein the washcoat coating is porous or gas permeable.
9. A substrate according to claim 1 , wherein the substrate is a metallic catalyst substrate.
10. A substrate according to claim 9 , wherein the substrate is a flow-through monolith.
11. A substrate according to claim 1 , wherein the fibrous or whisker-like material is a gamma alumina fiber.
12. A substrate according to claim 1 , wherein the washcoat coating is formed by applying a washcoat composition to the substrate and drying the washcoat composition, and the fibrous material forms 1-15 wt % of the washcoat composition.
13. A substrate according to claim 1 , wherein the washcoat coating is formed by applying a washcoat composition to the substrate and drying the washcoat composition, and the metal oxide forms up to 35 wt % of the washcoat composition.
14. A method of forming a substrate according to claim 1 , comprising applying to a substrate a slurry comprising a washcoat composition comprising a catalytic component, a metal oxide and a refractory fibrous or whisker-like material having an aspect ratio of length to thickness in excess of 5:1, and drying and firing the coated substrate to form the washcoat coating from the washcoat composition.
15. A slurry comprising a washcoat composition for use in the method of forming a solid catalyst carrier substrate coated with a surface area-enhancing washcoat coating according to claim 1 , which washcoat composition comprising a catalytic component, a metal oxide and a refractory fibrous or whisker-like material having an aspect ratio of length to thickness in excess of 5:1.
16. A substrate according to claim 1 , wherein the substrate is a static mixer.
17. A substrate according to claim 1 , wherein the substrate comprises a wire mesh device.
18. A substrate according to claim 1 , wherein the substrate comprises a plate.
19. A substrate according to claim 1 , wherein metal oxide is selected from the group consisting of silica, alumina, titania, a ceria-zirconia mixed oxide, and a ceria-zirconia-alumina blend.