Plasticzer in alkyl acrylate vinylidene chloride polymer

1. An article selected from a package, a container, a laminate, a sausage casing or a combination thereof comprising a monolayer blown film prepared from a composition including at least one vinylidene chloride polymer and at least one plasticizer present in an amount of from 3 to 9 parts by weight per hundred parts of polymer, and selected from ester plasticizers and combinations of ester plasticizer and epoxy plasticizer wherein at least one vinylidene chloride polymer comprises vinylidene chloride and at least one alkyl acrylate selected from methyl acrylate, ethyl acrylate, or butyl acrylate or a combination thereof in an amount of from 3.8 to 7.5 mole percent of the monomer content of the vinylidene chloride polymer from wherein the alkyl acrylate is present in an amount that results in at least 4 of the following characteristics:

(a) the crystallization temperature as determined by differential scanning calorimetry (DSC) is at most about 75° C.;

(b) the remelt temperature as determined by DSC is from 100° C. to 175° C.;

(c) the failure rate is at most about 150 per 10000 after having been heated to a temperature of from 75° C. to 145° C. for a period of from 20 minutes to 200 minutes:

(d) the oxygen permeability as determined by the procedures of ASTM D3985 is from 4.6×10E-17 m 3 .m/m 2 .sec.atm to 4.6×10E-13 m 3 .m/m 2 .sec.atm; and

(e) the glass transition temperature as determined by DSC of at most about 0° C.

2. The article of claim 1 wherein the alkyl acrylate is methyl acrylate or butyl acrylate and the alkyl acrylate is present in an amount from 4.2 to 6.5 mole percent of the vinylidene chloride polymer, and which results in all 5 of the following characteristics:

(a) the crystallization temperature is at most about 60° C.;

(b) the remelt temperature is from 100° C. to 175° C.;

(c) the failure rate is at most about 20 per 10000 after having been heated to a temperature of from 75° C. to 145° C. for a period of from 20 minutes to 200 minutes:

(d) the oxygen permeability is from 4.6×10E-17 m 3 .m/m 2 .sec.atm 2.3×10E-14 m 3 .m/m 2 .sec.atm; and

(e) the glass transition temperature of at most about −4° C.

3. The article of claim 1 wherein the film is blown using a double bubble process.

4. The article of claim 1 which is a sausage casing.

5. The article of any of claims 1 , 2 , 3 or 4 containing in addition to the vinylidene chloride polymer, less than 50 weight percent of total polymer of at least one thermoplastic polyurethane or copolymer of an alpha olefin and an alkyl ester of an unsaturated carboxylic acid, or a combination thereof.

6. The article of claim 5 containing in addition to the vinylidene chloride polymer, at least one copolymer of an alpha olefin and an alkyl ester of an unsaturated carboxylic acid selected from ethylene/methyl acrylate copolymer, ethylene/butyl acrylate copolymers and combinations thereof.

7. A process of forming the film in claim 1 by blowing a monolayer film using a double-bubble method comprising steps of (a) supplying a composition comprising at least one vinylidene chloride polymer, and at least one plasticizer wherein at least one vinylidene chloride polymer comprises vinylidene chloride and at least one alkyl acrylate selected from methyl acrylate, ethyl acrylate, or butyl acrylate or a combination thereof in an amount of from 3.8 to 7.5 mole percent of the monomer content of the vinylidene chloride polymer and wherein the plasticizer is present in an amount of from 3 to 9 parts by weight per hundred parts of polymer; (b) extruding the composition through an annular die into a tube form; (a) quenching the extruded tube in a cold water bath; and (d) collapsing the tube into a tape form.

8. The process of claim 7 wherein the process additionally comprises (e) reheating the collapsed tape in a warm tank, (f) sizing the tube to attain a desired width of the collapsed tape using a volume of fluid held inside the extruded tube, (g) forming a bubble of the composition, (h) collapsing the film bubble, and (i) winding the resulting film onto at least one roll.

9. The process of claim 8 additionally comprising a step preceding step (a) of polymerizing the vinylidene chloride and alkyl acrylate monomer together at a rate that exceeds the rate of polymerization of the vinylidene chloride and vinyl chloride under the same conditions.