Benzoxazine compounds derivated from phenolphthalein having flame-retardant properties and a process for their preparation
The instant invention relates to 3,3′-bis(3,4-dihydro-3-phenyl-2H-1,3-benzoxazin-6-yl)-1(3H)-isobenzofuranone and analogues based on phenolphthalein, formaldehyde and a primary amine. Such compounds are, when cured to form polymeric networks, difficultly inflammable and resistant to high temperatures. Such compounds may especially be used in the production of printed wiring boards.
1. A polymeric resin obtained by curing at a temperature above 100° C. a compound of the formula
wherein R is, independently from one another, allyl, unsubstituted or substituted phenyl, unsubstituted or substituted C 1 -C 8 -alkyl or unsubstituted or substituted C 3 -C 8 -cycloalkyl.
2. The polymeric resin according to claim 1 , wherein both substituents R are the same.
3. The polymeric resin according to claim 1 , wherein R is phenyl.
4. The polymeric resin according to claim 1 , wherein R is substituted by one to four substituents selected from the group consisting of amino, C 1 -C 4 -alkyl and allyl.
5. The polymeric resin according to claim 1 , wherein the compound of formula (I) is obtained by: (i) reacting, under removal of water, and in the presence of a solvent and under pressure of up to about 100 psi, phenolphthalein with formaldehyde and a primary amine, whereby the molar ratio of phenolphthalein and formaldehyde is from 1:4.5 to 1:5 and the molar ratio of phenolphthalein and the primary amine groups is from 1:2.1 to 1:2.2.
6. The polymeric resin according to claim 5 , whereby the primary amine is a compound of the formula RNH 2 (II), wherein R is allyl, unsubstituted or substituted phenyl, unsubstituted or substituted C 1 -C 8 -alkyl or unsubstituted or substituted C 3 -C 8 -cycloalkyl.
7. A process for preparing a flame retarded casting or laminate by thermally curing a compound of the formula
wherein R is, independently from one another, allyl, unsubstituted or substituted phenyl, unsubstituted or substituted C 1 -C 8 -alkyl or unsubstituted or substituted C 3 -C 8 -cycloalkyl and optionally an additive selected from reinforcement fibers, a plasticizer, carbon black, graphite, a filler, a dyestuff, micro hollow spheres, a metal powder and a mixture thereof.
8. A laminating composition consisting of 30 to 80% by weight of a compound of the formula
wherein R is, independently from one another, allyl, unsubstituted or substituted phenyl, unsubstituted or substituted C 1 -C 8 -alkyl or unsubstituted or substituted C 3 -C 8 -cycloalkyl and 0.1 to 50% by weight of ferrocene, and optionally a solvent or solvent mixture, a catalyst, a flame retardant, an epoxy resin, a filler or combinations thereof.