Maleated and oxidized fatty acids
View Patent ↗An oxidized and maleated fatty acid composition, especially an oxidized and maleated tall oil fatty acid-containing product useful in formulating corrosion inhibitors and for use as an emulsifier, especially for petroleum-related applications.
1. A composition useful for inhibiting corrosion or for use as an emulsifier in preparing invert water-in-oil emulsions comprising maleated and oxidized tall oil fatty acids, the oxidized tall oil fatty acids having crosslinks of an ether linkage between hydrocarbon chains of the oxidized tall oil fatty acids obtained by sparging air or oxygen through heated tall oil fatty acids heated to a temperature above 150 ° C. wherein the composition comprises dimers, trimers, or mixtures thereof of the maleated and oxidized tall oil fatty acids.
2. The composition of claim 1 wherein the fatty acids comprise a tall oil composition containing a tall oil rosin acid.
3. The composition of claim 1 or 2 wherein the maleated fatty acids have from about 2% to about 25% by weight of maleic anhydride, fumaric acid, acrylic acid, methacrylic acid or a mixture thereof.
4. The composition of claim 3 wherein the sparging is conducted for 10.5 to 16 hours.
5. A method for reducing corrosion associated with a metal surface comprising contacting said surface with a corrosion inhibiting amount of the composition of claim 1 or 2 .
6. A method for reducing corrosion associated with a metal surface comprising contacting said surface with a corrosion inhibiting amount of the composition of claim 3 .
7. A method for making an emulsion from water and an oil comprising mixing with the water and the oil an emulsifying amount of the composition of claim 1 or 2 .
8. A method for making an emulsion from water and an oil comprising mixing with the water and the oil an emulsifying amount of the composition of claim 3 .
9. A method of preparing a composition of claim 1 useful for inhibiting corrosion or for use as an emulsifier in preparing invert water-in-oil emulsions comprising maleating and oxidizing tall oil fatty acids, wherein the oxidizing occurs by sparging air or oxygen through heated tall oil fatty acids heated to a temperature above 150 ° C. to produce a composition comprising dimers, trimers, or mixtures thereof of the maleated and oxidized tall oil fatty acids.
10. The method of claim 9 wherein the tall oil fatty acids are reacted with from about 2% to about 25% by weight of maleic anhydride, fumaric acid, acrylic acid, methacrylic acid or a mixture thereof.
11. The method of claim 10 wherein the tall oil fatty acids comprise a tall oil composition containing a tall oil rosin acid.
12. The method of claim 10 wherein the sparging is conducted for 10.5 to 16 hours.
13. A composition useful for inhibiting corrosion or for use as an emulsifier in preparing invert water-in-oil emulsions comprising maleated and oxidized tall oil fatty acids, the oxidized tall oil fatty acids having crosslinks of an ether linkage between hydrocarbon chains of the oxidized tall oil fatty acids obtained by sparging air or oxygen through heated tall oil fatty acids heated to a temperature above 150 ° C. wherein the composition comprises one or more of the following structures: