WATER SOLUBLE CONCENTRIC MULTI-WALL CARBON NANO TUBES
The present invention relates to water soluble carbon nano tubes (WSNT) which have been made function by functionalizing with carboxylic acid groups. The carbon nano tubes are isolated from hydrocarbon wax soot and then functionalized by oxidation treatment with an oxidizing agent. The WSNT can contain a pharmaceutical composition for release by a biological degradation agent of the WSNT for example E coli.
1 . A method of making a water soluble concentric multi-wall carbon nano tube comprising:
a) heating a hydrocarbon wax to a temperature of between about 500 degree C. and 800 degree C. under conditions sufficient to produce carbon soot containing carbon nano tubes;
b) purifying the soot to isolate the nano tubes;
c) oxidatively treating the nano tubes to remove amorphous carbon and produce hydrophilic carboxylic acid groups on the sidewall surface of the nano tubes.
2 . A method according to claim 1 wherein the nano tubes are oxidativly treated with one or more oxidizing agent selected from the group consisting of:
a) nitric acid;
b) a per acid;
c) ammonium ceric nitrate.
3 . A method according to claim 1 wherein the hydrocarbon wax is selected from the group comprising:
a) an insect wax;
b) an animal wax;
c) a mineral wax;
d) a synthetic wax;
e) a vegetable wax; and
f) a petroleum wax.
4 . A method according to claim 3 wherein the petroleum wax is paraffin.
5 . A method according to claim 3 wherein the insect wax is bees wax.
6 . A method according to claim 1 wherein the method further comprises incorporating a pharmaceutical composition within the nano tubes.
7 . A method according to claim 1 wherein the soot is purified by solvent washing.
8 . A method according to claim 2 wherein the oxidative agent is nitric acid.
9 . A method according to claim 8 wherein the nitric acid is mixed with one or composition selected from the group comprising:
a) sulfuric acid;
b) sodium meta bisulfate; and
c) a per acid like perboric acid, peroxy sulfuric acid, hydrogen peroxide and its other derivatives containing peroxo group.
10 . A method according to claim 2 wherein the oxidative agent is a per acid.
11 . A method according to claim 10 wherein the per acid is combined with nitrogen dioxide.
12 . Soot produced concentric multi-wall carbon nano tubes that have been made water soluble by the addition of carboxylic acid groups to the sidewall surface.
13 . Carbon nano tubes according to claim 12 with a diameter of from about 30 to 60 nm.
14 . Carbon nano tubes according to claim 12 which further comprises a selected pharmaceutical within the nano tubes.
15 . Carbon nano tubes according to claim 14 wherein the selected pharmaceutical is in a liquid form.
16 . Carbon nano tubes according to claim 14 wherein the selected pharmaceutical is selected from the group comprising antibiotics, and photodynamic therapeutic reagents.
17 . A method of delivering a pharmaceutical composition to a patient in need thereof comprising administering to the patient the pharmaceutical composition contained in a soot produced concentric multi-walled carbon nano tubes that has been made water soluble by the addition of carboxylic acid groups to the sidewall surface of the nano tube.