Developer rolls having a tuned resistivity
View Patent ↗Developer roll having a conductive or semi-conductive soft rubber core and a coating deposited in the soft rubber core wherein the coating has a conductive agent. The outer surface of the soft rubber core is modified before the coating is deposited onto the outer surface of the soft rubber core. Methods for making the same.
1. A developer roll having a tuned resistivity, comprising:
a conductive or semi-conductive soft rubber core having an outer surface including an —OH rich surface layer, wherein the soft rubber core is molded on a metal shaft; and
a coating deposited on the outer surface of the soft rubber core, wherein the coating comprises a polyurethane prepolymer and a conductive agent, the polyurethane prepolymer including an isocyanate portion and a polyol portion, the —OH rich surface layer of the soft rubber core chemically bonded with the isocyanate portion of the polyurethane prepolymer adhering the coating to the outer surface of the soft rubber core,
wherein the isocyanate portion comprises a caprolactone-H 12 MDI urethane.
2. The developer roll of claim 1 , wherein the conductive agent comprises one or more ionic additives or an inherently conductive polymer (ICP).
3. The developer roll of claim 2 , wherein the ionic additive is selected from the group consisting of: LiPF 6 , LiAsF 6 , LiN(SO 2 CF 3 ) 2 , LiC(SO 2 CF 3 ) 3 , LiPF 3 (C 2 F 5 ), Cs(CF 3 COCH 2 COCF 3 ), KPF 6 , NaPF 6 , CuCl 2 , FeCl 3 , FeCl 2 , Bu 4 NPF 6 , Bu 4 NSO 3 CF 3 , Bu 4 NCl, and Bu 4 NBr.
4. The developer roll of claim 1 , wherein the developer roll has a coating resistivity of about 5.0×10 10 to about 3.0×10 12 ohm-cm at 15.6° C./20% relative humidity (RH).
5. The developer roll of claim 4 , wherein the coating has a thickness of from about 50 micrometers to about 100 micrometers.
6. The developer roll of claim 1 , wherein the coating further comprises one or more curative additives, wherein the curative additives are selected from the group consisting of: polycaprolactone polyols, polyether polyols, polyester polyols, aliphatic-polycarbonate polyols, polybutadiene diol, polydimethylsiloxane polyols, and polydimethylsiloxane diamines.
7. The developer roll of claim 6 , wherein the curative additive comprises an alkoxylated trimethylolpropane polyether polyol.
8. The developer roll of claim 1 , wherein the soft rubber core comprises one or more of the rubbers selected from the group consisting of: silicone rubber, nitrile rubber, ethylene propylene (EP) copolymers, polybutadiene, styrene-co-butadiene, isoprene rubber, and a blend of one or more of the rubbers.
9. The developer roll of claim 1 , wherein the polyol portion is selected from the group consisting of a polyether, polyester and polybutadiene system.
10. The developer roll of claim 1 , wherein the soft rubber core further comprises one or more conductive agents selected from the group consisting of: carbon black, carbon fibers and graphite.
11. The developer roll of claim 1 , wherein the coating has a thickness of from about 10 micrometers to about 100 micrometers.
12. The developer roll of claim 1 , wherein the conductive agent comprises cesium hexafluoroacetylacetonate.
13. The developer roll of claim 1 , wherein the isocyanate portion further comprises a caprolactone-TDI urethane, and wherein the conductive agent comprises cesium hexafluroroacetylacetonate.
14. A developer roll, comprising:
a metal shaft;
a conductive or semi-conductive soft rubber core having an outer surface including an —OH rich surface layer, wherein the soft rubber core is disposed on the metal shaft; and
a coating deposited on the outer surface of the soft rubber core, wherein the coating comprises a polyurethane prepolymer and a conductive agent, the polyurethane prepolymer including an isocyanate portion and a polyol portion, the —OH rich surface layer of the soft rubber core chemically bonded with the isocyanate portion of the polyurethane prepolymer adhering the coating to the outer surface of the soft rubber core,
wherein the isocyanate portion comprises a caprolactone-H 12 MDI urethane.
15. The developer roll of claim 14 , wherein the conductive agent comprises cesium hexafluoroacetylacetonate.
16. The developer roll of claim 14 , wherein the isocyanate portion further comprises a caprolactone-TDI urethane.