BIAXIALLY DRAWN ADHESIVE TAPES AND METHOD FOR PRODUCING THE SAME
A method of producing a film adhesive tape, characterized in that a composite comprising at least one extruded backing film layer and a pressure sensitive adhesive layer on one side of the backing film layer is biaxially drawn.
1 . A method of producing an adhesive tape, said method comprising simultaneously biaxially drawing a composite comprising at least one extruded backing film layer and a pressure sensitive adhesive layer adhered directly or indirectly on one side of the backing film layer.
2 . The method of claim 1 , wherein the composite comprises a primer layer between the backing film layer and the pressure sensitive adhesive layer.
3 . The method of claim 1 , wherein the composite comprises a release layer on a side of the backing film layer opposite the side of the backing film layer to which said pressure sensitive adhesive layer is adhered.
4 . The method of claim 1 , wherein the backing film layer of the adhesive tape is heat-set.
5 . The method of claim 1 , which further comprises heat-setting the composite after drawing.
6 . The method of claim 1 , wherein the pressure sensitive adhesive is applied to the backing film layer by melt coating.
7 . The method of claim 1 , wherein the pressure sensitive adhesive is applied to the backing film layer by coextrusion.
8 . The method claim 1 , wherein the pressure sensitive adhesive is applied by lamination to the backing film layer or to the primer layer prior to drawing.
9 . The method of at claim 1 , which further comprises producing all layers of the composite by a solvent-free procedure from a melt.
10 . The method of claim 1 , wherein the pressure sensitive adhesive is crosslinked chemically or by means of high-energy radiation.
11 . The method of claim 1 , wherein the drawing is carried out on a unit with linear motor technology.
12 . The method of claim 1 , which further comprises supplying the composite after drawing in an in-line operation to a roll winder or to a slitting machine.
13 . The method of claim 1 , which yields an overall draw ratio of at least 1:40.
14 . The method of claim 1 , wherein a ratio of a draw ratio in a machine direction to a draw ratio in a transverse a direction is a value of above 0.9.
15 . The method of claim 1 , which further comprises winding the adhesive tape onto paperboard cores with an elastic foam lining.
16 . An adhesive tape comprising a simultaneously biaxially drawn composite, wherein the composite comprises at least one extruded backing film layer and a pressure sensitive adhesive layer that is adhered directly or indirectly on one side of the backing film layer.
17 . The adhesive tape of claim 16 , wherein the backing film layer comprises at least one nucleating agent.
18 . The adhesive tape of claim 16 , wherein the backing film layer is composed predominantly of isotactic polypropylene.
19 . The adhesive tape of claim 16 , wherein the backing film layer comprises polypropylene having a melt index of from 1 to 10 g/10 min.
20 . The adhesive tape of claim 16 , wherein the backing film layer is stretched such that the stress at 10% elongation in a machine direction is at least 50 N/mm 2 .
21 . The adhesive tape of claim 16 , wherein the backing film layer is stretched such that the tensile strength in a machine direction is at least 160 N/mm 2 .
22 . The adhesive tape of claim 16 , wherein the backing film layer is composed predominantly of polyethylene terephthalate.
23 . The adhesive tape of claim 16 , wherein the pressure sensitive adhesive layer comprises natural rubber.
24 . The adhesive tape of claim 16 , wherein the pressure sensitive adhesive layer comprises at least one styrene-isoprene block copolymer.
25 . The adhesive tape of claim 16 , wherein the pressure sensitive adhesive layer comprises at least one resin.
26 . The adhesive tape of claim 16 , which exhibits a bond strength on steel of at least 1.3 N/cm.
27 . The adhesive tape of claim 16 , which has a thickness of at least 35 mm.
28 . The adhesive tape of claim 16 , wherein the backing film layer is stretched such that the stress at 10% elongation in machine direction is at least 70 N/mm 2 .
29 . The adhesive tape of claim 28 , wherein the backing film layer is stretched such that the stress at 10% elongation in machine direction is at least 100 N/mm 2 .
30 . The adhesive tape of claim 21 , wherein the backing film layer is stretched such that the tensile strength in a machine direction is at least 190 N/mm 2 .
31 . The adhesive tape of claim 30 , wherein the backing film layer is stretched such that the tensile strength in a machine direction is at least 220 N/mm 2 .
32 . The adhesive tape of claim 16 , which exhibits a bond strength on steel of at least 1.6 N/cm.
33 . The adhesive tape of claim 27 , which has a thickness of between 35 mm and 65 mm.
34 . A method of producing an adhesive bond comprising adhering an adhesive tape according to claim 16 to a substrate.