Wear resistant materials
View Patent ↗A hard phase material is provided for increasing the hardness of a matrix material and improving the wear resistance thereof. The hard phase material is an aluminum boride material having the structure AlB 8-16 . The aluminum boride hard phase may be incorporated into a matrix material by mixing particulate aluminum boride with the matrix material and through precipitation of aluminum boride from the matrix material. Materials including the aluminum boride hard phase may be used in coating applications to provide a hard and wear resistant coating. Aluminum boride hard phase may also be incorporated into metallurgical products to improve the hardness and wear resistance of the metallurgical products.
1. A method for forming a wear resistant material comprising aluminum boride of the general formula AlB 8-16 comprising:
(a) supplying a metallic system comprising (Fe 52.3 Mn 2 Cr 19 Mo 2.5 W 1.7 B 16 C 4 Si 2.5 );
(b) adding up to 50 atomic percent of aluminum and boron as separate ingredients to said metallic system, forming a supersaturated solution;
(c) melting said metallic system and precipitating aluminum boride from a liquid phase of said metallic system including said aluminum and said boron to form said wear resistant material, wherein said metallic system forms a matrix in which said aluminum boride is incorporated, and at least 24 atomic percent of said wear resistant material comprises aluminum and boron.
2. The method of claim 1 , further comprising atomizing said metallic system into particulate form.
3. The method of claim 2 wherein said step of atomization includes one of a gas, water or centrifugal atomization method.
4. The method of claim 1 , wherein said wear resistant material has the following composition:
[(Fe 52.3 Mn 2 Cr 19 Mo 2.5 W 1.7 B 16 C 4 Si 2.5 ) 100-x-y +(AlB 12 ) x ±Al y ]
wherein x is in the range of 10 and 41 and y is in the range of 0 to 7.
5. A method for forming a wear resistant material comprising aluminum boride of the general formula AlB 8-16 comprising:
(a) supplying a metallic system comprising an iron based alloy including manganese, chromium, molybdenum, tungsten, carbon, silicon and boron,
(b) adding up to 50 atomic percent of boron and aluminum to said iron based alloy, forming a supersaturated solution wherein said aluminum reacts with said boron; and
(c) melting said metallic system and precipitating aluminum boride from a liquid phase of said metallic system including said boron and aluminum to form said wear resistant material, wherein said metallic system forms a matrix in which said aluminum boride is incorporated and said wear resistant material has the following composition:
[(Fe 52.3 Mn 2 Cr 19 Mo 2.5 W 1.7 B 16 C 4 Si 2.5 ) 100-x-y +(AlB 12 ) x +Al y ],
wherein x is in the range of 10 and 41 and y is in the range of 0 to 7.
6. The method of claim 5 wherein said metallic material has a hardness “x”, and upon forming said aluminum boride said hardness increases to a value “y” wherein y>x, and wherein upon incorporation of aluminum, said hardness increases to a value “z”, wherein z>y.
7. The method of claim 5 , further comprising atomizing said metallic system into particulate form.
8. A method for forming a wear resistant material comprising aluminum boride of the general formula AlB 8-16 comprising:
(a) supplying a metallic system comprising (Fe 52.3 Mn 2 Cr 19 Mo 2.5 W 1.7 B 16 C 4 Si 2.5 );
(b) adding up to 50 atomic percent of aluminum and boron as separate ingredients to said metallic system, forming a supersaturated solution;
(c) melting said metallic system and precipitating aluminum boride from a liquid phase of said metallic system including said aluminum and said boron to form said wear resistant material, wherein said metallic system forms a matrix in which said aluminum boride is incorporated.
9. The method of claim 8 , further comprising atomizing said metallic system into particulate form.
10. The method of claim 9 , wherein said step of atomization includes one of a gas, water or centrifugal atomization method.
11. The method of claim 9 , wherein said wear resistant material has the following composition:
[(Fe 52.3 Mn 2 Cr 19 Mo 2.5 W 1.7 B 16 C 4 Si 2.5 ) 100-x-y +(AlB 12 ) x +Al y ]
wherein x is in the range of 10 and 41 and y is in the range of 0 to 7.
12. The method of claim 7 , wherein said step of atomization includes one of a gas, water or centrifugal atomization method.