Systems and methods of making molded composite blocks
Provided are filtration matrixes formed from adsorptive media, such as activated carbon, and polymeric binder for use in water filtration systems. A first aspect of the invention provides methods of making a filtration matrix comprising: mixing an adsorptive media with a polymeric binder to form a mixture; impulse filling a mold with the mixture; and processing the mixture to form the filtration matrix. Filtration matrixes formed from this method are also provided. Another aspect includes methods of making a filtration matrix comprising: mixing adsorptive media with a polymeric binder to form a mixture; filling a mold with the mixture; and applying heat and pressure the mixture to form the filtration matrix, wherein the step of applying pressure to the mixture comprises compressing the mixture until a desired final shape of the filtration matrix is obtained.
1. A method of making a filtration matrix comprising:
mixing an adsorptive media with a polymeric binder to form a mixture, the adsorptive media comprising activated carbon suitable for the removal of contaminants from water;
impulse filling a mold with the mixture to an uncompressed density, impulse filling comprises administering impulses at a rate in the range of 6 to 120 impulses per minute; and
following impulse filling, heating and compressing the mixture to form the filtration matrix with a VOC capacity according to NSF-53 of 20 gal/in 3 or greater.
2. The method of claim 1 , wherein the rate is about 20 impulses per minute.
3. The method of claim 1 , wherein the mixture has a maximum uncompressed density, and the mixture after the mold is filled is at least 90% of the maximum uncompressed density.
4. The method of claim 3 , wherein the mixture after the mold is filled is at least 95% of the maximum uncompressed density.
5. The method of claim 1 , wherein heating comprises heating the mold to a temperature in the range of 160° C. to 250° C.
6. The method of claim 1 , further comprising providing a mold that is tapered to facilitate removal of the filtration matrix from the mold.
7. The method of claim 1 , wherein the adsorptive media further comprises a lead-removal media.
8. The method of claim 1 , wherein the binder comprises ultra high molecular weight polyethylene.
9. The method of claim 1 , wherein the impulse filling is used to fill a plurality of molds, and wherein a plurality of filtration matrixes is formed.
10. The method of claim 9 , wherein a standard deviation of the average weight of the plurality of filtration matrixes is no greater than 10% of the average weight.
11. The method of claim 10 , wherein the standard deviation is no greater than 5% of the average weight.
12. The method of claim 1 , wherein heating and compressing are done substantially simultaneously.
13. The method of claim 1 , wherein heating occurs before compressing.
14. The method of claim 1 , wherein compressing occurs before heating.
15. The method of claim 1 , wherein compressing comprises applying compressive force axially to the mixture.
16. The method of claim 1 , wherein the impulse filling comprises an indirect force on the mold such that the table to which the mold is secured receives a force directly.
17. A method of making a filtration matrix comprising:
mixing an adsorptive media with ultra high molecular weight polyethylene to form a mixture comprising the adsorptive media in an amount in the range of 65 to 90% by weight and ultra high molecular weight polyethylene in an amount in the range of 35 to 10% by weight, the adsorptive media comprising an activated carbon suitable for the removal of contaminants from water;
impulse filling a mold with the mixture to an uncompressed density, impulse filling comprises administering impulses at a rate in the range of 6 to 120 impulses per minute;
following impulse filling, heating the mold to a temperature in the range of 160° C. to 200° C.;
compressing the mixture until a fixed length of the filtration matrix is obtained; and
cooling the mold;
wherein the filtration matrix has a VOC capacity according to NSF-53 of 20 gal/in 3 or greater.
18. The method of claim 17 , wherein the impulse filling comprises an indirect force on the mold such that the table to which the mold is secured receives a force directly.