Polyurethane composite materials
View Patent ↗Polymeric composite materials, particularly highly filled polyurethane composite materials are described herein. Such highly filled polyurethane composite materials may be formed by reaction and extrusion of one or more polyols, one or more di- or poly-isocyanates, and from about 45 to about 85 weight percent of inorganic filler such as fly ash. Certain polyols, including plant-based polyols can be used. Certain composite materials also contain chain extenders and/or crosslinkers. The polyurethane composite material may also contain fibers such as chopped or axial fibers which further provide good mechanical properties to the composite material. Shaped articles containing the polyurethane composite material have been found to have good mechanical properties, such that the shaped articles are suitable for building applications.
1. A polyurethane composite material comprising:
a polyurethane formed by reaction of a reaction mixture of:
one or more monomeric or oligomeric poly- or di-isocyanates; and
a first polyol, which is a rigid polyol, having a first hydroxyl number in the range of about 320 mg KOH/g to about 600 mg KOH/g; and
a second polyol having a second hydroxyl number, wherein the second hydroxyl number is at least about 20 mg KOH/g and is substantially less than the first hydroxyl number;
wherein the first polyol and the second polyol are plant based polyester polyols;
water in an amount that provides a composite material having a density of about 30 lbs/ft 3 to about 85 lbs/ft 3 ; wherein the mixture is substantially free of halogenated hydrocarbons;
wherein the ratio of the first polyol to the second polyol is about 3 to about 20;
about 40 to about 85 weight percent inorganic filler, wherein the inorganic filler comprises coal ash; and
reinforcing fiber having a length in the range of 0.125 inches to about 1 inch.
2. The polyurethane composite material of claim 1 , wherein the material comprises about 65 to about 75 weight percent inorganic filler.
3. The polyurethane composite material of claim 1 , wherein the material comprises about 60 to about 85 weight percent inorganic filler.
4. The polyurethane composite material of claim 1 , wherein the material comprises about 65 to about 85 weight percent inorganic filler.
5. The polyurethane composite material of claim 1 , wherein the material comprises fly ash.
6. The polyurethane composite material of claim 1 , wherein the material comprises about 0.01 wt % to about 0.5 wt % of the at least one coupling agent.
7. A polyurethane composite material comprising:
a polyurethane formed by reaction of a reaction mixture comprising:
one or more monomeric or oligomeric poly- or di-isocyanates;
a first polyol, which is a rigid polyol, having a first hydroxyl number in the range of about 320 mg KOH/g to about 600 mg KOH/g; and
a second polyol having a second hydroxyl number, wherein the second hydroxyl number is at least about 20 mg KOH/g and is less than the first hydroxyl number;
wherein the first polyol and the second polyol are plant based polyester polyols;
a blowing agent;
wherein the blowing agent is water, which is present at a concentration of less than about 0.4 % based upon the weight of the composite material;
wherein the ratio of the first polyol to the second polyol is about 3 to about 20;
about 60 to about 85 weight percent of an inorganic filler, based upon the weight of the composite material, wherein the inorganic filler comprises coal ash;
wherein the reaction mixture is substantially free of halogenated hydrocarbons;
an ultraviolet light stabilizer;
about 0.1 to about 10 weight percent of a reinforcing fiber based upon the weight of the composite material;
wherein the reinforcing fiber has a length in the range of 0.125 inches to about 1 inch;
wherein the composite material has a density of about 65 lbs/ft 3 to about 85 lbs/ft 3 .
8. The polyurethane composite material of claim 7 , wherein the material comprises about 65 to about 75 weight percent of the inorganic filler.
9. The polyurethane composite material of claim 7 , wherein the material comprises about 65 to about 85 weight percent of the inorganic filler.
10. The polyurethane composite material of claim 7 , wherein the material comprises fly ash.
11. The polyurethane composite material of claim 7 , wherein the material additionally comprises chopped fibers.
12. The polyurethane composite material of claim 11 , wherein the chopped fibers comprises chopped fiber glass and chopped basalt fiber.
13. The polyurethane composite material of claim 7 , further comprising axially oriented fiber rovings disposed on, in, or beneath the surface of the composite.
14. The polyurethane composite material of claim 7 , wherein the reaction mixture further comprises at least one of ethylene glycol, 1,4-butane diol, trimethylolpropane, glycerol, and sorbitol.
15. The polyurethane composite material of claim 7 , wherein the materially comprises a chain extender, the chain extender being an organic compound having two or more hydroxyl groups.
16. The polyurethane composite material of claim 7 , wherein a chain extender is reacted with the one or more monomeric or oligomeric poly- or di-isocyanates.
17. A method of forming a polyurethane composite material, the method comprising:
providing a first polyol, which is a rigid polyol, having a first hydroxyl number in the range of about 320 mg KOH/g to about 600 mg KOH/g;
providing a second polyol, which is a flexible polyol, having a second hydroxyl number, wherein the second hydroxyl number is at least about 20 mg KOH/g and is substantially less than the first hydroxyl number;
wherein the ratio of rigid polyol to flexible polyol is about 3 to about 20;
wherein the first polyol and the second polyol are plant based polyester polyols;
providing at least one poly or di-isocyanate;
providing about 45 to about 85 weight percent of an inorganic filler based upon the weight of the composite material;
providing a blowing agent consisting essentially of water at a concentration of less than about 0.4% based upon the weight of the composite material;
wherein the mixture is substantially free of halogenated hydrocarbons;
extruding the first polyol, the second polyol, the at least one poly or di-isocyanate, and the inorganic filler into an extruded mixture; and
containing the extruded mixture in a forming device;
wherein the resulting polyurethane composite material has a density in the range of about 30 lbs/ft 3 to about 85 lbs/ft.
18. The method of claim 17 , further comprising placing the extruded mixture in a mold.
19. The method of claim 18 , further comprising shaping the extruded mixture in the mold.
20. The method of claim 19 , wherein the mold is formed by one or more belts of a forming device.
21. The method of claim 17 , further comprising mixing the at least one polyol with a solvent.
22. The method of claim 21 , wherein the solvent comprises about to 2 to about 10 wt % of one or more solvents selected from the group consisting of pentane, hexane, and ethyl acetate.