Manufacturing method of ladder-like phosphorous-containing polysilsesquioxanes nanocomposite material
View Patent ↗A manufacturing method of ladder-like phosphorus-containing polysilsesquioxanes nanocomposite material is disclosed. The method uses a reaction between ladder-like phosphorus-containing polysilsesquioxanes and modified epoxy. Besides improved char yield and limiting oxygen index, thermal degradation rate of the nanocomposite material is lowered dramatically so that the nanocomposite material possesses excellent flame retardance and thermal stability. Moreover, optical transparency of the nanocomposite material according to the present invention is still good, not being reduced by increased amount of polysilsesquioxanes. Thus the nanocomposite material is applied to decorative paints or protective paints.
1. A manufacturing method of ladder-like phosphorus-containing polysilsesquioxanes nanocomposite material comprising the steps of:
adding epoxy resin containing siloxane group into ladder-like phosphorus-containing polysilsesquioxanes, together with tetraethoxysilane and catalyst for performing hydrolysis reaction and condensation reaction adding curing agent; and
taking a curing process, a drying process, and a sintering process.
2. The method as claimed in claim 1 , wherein the epoxy resin containing siloxane group is IPTS (3-Isocyanatopropyltriethoxysilane)-epoxy resin.
3. The method as claimed in claim 2 , wherein a manufacturing method of the IPTS-epoxy resin comprising the steps of
dissolving DGEBA (Diglycidylether of bisphenol A) epoxy in tetrahydrofuran (THF);
adding IPTS into the DGEBA type epoxy solution;
adding catalyst into the solution to allow a reaction to take place; and
getting IPTS-epoxy resin solution.
4. The method as claimed in claim 3 , wherein the catalyst comprising triethanolamine.
5. The method as claimed in claim 1 , wherein the catalyst is hydrogen chloride.
6. The method as claimed in claim 1 , wherein the curing agent is 4,4-Methylenedianline (DDM).
7. The method as claimed in claim 1 , wherein a concentration of the ladder-like phosphorus-containing polysilsesquioxanes is 9 wt %.
8. The method as claimed in claim 1 , wherein the ladder-like phosphorus-containing polysilsesquioxanes nanocomposite material is composite material in nano-scale.
9. The method as claimed in claim 1 , wherein the ladder-like phosphorus-containing polysilsesquioxanes nanocomposite material is amorphous.