Flame retardant thermoplastic molding composition

1. A thermoplastic molding composition comprising

A) 60 to 99 percent by weight (pbw) aromatic poly(ester) carbonate having a weight-average molecular weight of at least 25,000,

B) 1 to 40 pbw (co)polyester having an intrinsic viscosity from 0.94 deciliter/gram to 2.5 deciliter/gram, wherein the weight of A) and B) totals 100 parts (100 parts resin),

C) 1 to 20 parts per 100 parts resin (phr) graft (co)polymer having a core-shell morphology, comprising a grafted shell that contains polymerized alkyl(meth)acrylate and a composite rubber core that contains interpenetrated and inseparable polyorganosiloxane and poly(meth)alkyl acrylate where the weight ratio of polyorganosiloxane/poly(meth)alkylacrylate/grafted shell is 70-90/5-15/5-15,

D) 2 to 20 phr phosphorus-containing compound,

E) 0.1 to 2 phr fluorinated polyolefin and

F) 0.1 to 15 phr zinc borate having average particle diameter of 5 to 9 microns.

2. The composition of claim 1 wherein said aromatic poly(ester) carbonate is a homopolycarbonate based on bisphenol A.

3. The composition of claim 1 wherein said (co)polyester is polyethylene terephthalate.

4. The composition of claim 1 wherein said graft (co)polymer is present in an amount of 2 to 15 phr.

5. The composition of claim 1 wherein said phosphorous compound is a member selected from the group consisting of phosphoric acid ester and phosphonic acid ester.

6. The composition of claim 5 wherein said member conforms structurally to formula (IV)

wherein

R 1 , R 2 , R 3 and R 4 independently one of the others, each represents C 1 - to C 8 -alkyl, or C 5 - 6 -cycloalkyl, C 6 - 20 -aryl or C 7 - 12 -aralkyl,

n independently one of the others denotes 0 or 1,

q denotes 0.5 to 30, and

X is a mono- or poly-nuclear aromatic radical having from 6 to 30 carbon atoms, or an aliphatic radical having from 2 to 30 carbon atoms.

7. The composition of claim 1 wherein the fluorinated polyolefin is present in an amount of 0.2 to 1 phr.

8. The composition of claim 1 wherein said zinc borate is present in an amount of 1 to 10 phr.

9. A thermoplastic molding composition comprising

A) 70 to 95 pbw aromatic polycarbonate carbonate having a weight-average molecular weight of at least 26,000 g/mol.,

B) 5 to 30 pbw of polyethylene terephthalate having an intrinsic viscosity from 0.94 deciliter/gram to 2.5 deciliter/gram, wherein the weight of A) and B) totals 100 parts (100 parts resin),

C) 2 to 15 phr graft (co)polymer having a core-shell morphology, comprising a grafted shell that contains polymerized methylmethacrylate and a composite rubber core that contains interpenetrated and inseparable polyorganosiloxane and polyalkyl acrylate components, where the weight ratio of polyorganosiloxane/polyalkyl acrylate/polymerized methylmethacrylate is 70-90/5-15/5-15,

D) 5 to 15 phr of a phosphorus-containing compound conforming structurally to formula (IV)

wherein

R 1 , R 2 , R 3 and R 4 independently one of the others, each represents C 1 - to C 8 -alkyl, or C 5 - 6 -cycloalkyl, C 6 - 20 -aryl or C 7 - 12 -aralkyl,

n independently one of the others denotes 0 or 1,

q denotes 0.5 to 30, and

X is a mono- or poly-nuclear aromatic radical having from 6 to 30 carbon atoms, or an aliphatic radical having from 2 to 30 carbon atoms,

E) 0.2 to 1 phr fluorinated polyolefin and

F) 1 to 10 phr zinc borate having average particle diameter of 5 to 9 microns.

10. The composition of claim 9 wherein the zinc borate conforms to the general chemical formula mZnO.nB2O3.xH2O and where the ratio of x/m/n is 0-7/1-5/2-6.

11. The composition of claim 9 wherein the average particle diameter is 4 to 6 microns.

12. The composition of claim 9 wherein the average particle diameter is 8-10 microns.

13. The composition of claim 1 further containing at least one member selected from the group consisting of lubricant, mold-release agent, nucleating agent, antistatic, thermal stabilizer, hydrolytical stabilizer, light stabilizer, colorant, pigment, filler, reinforcing agent, flame proofing agent other than component D), and flame proofing synergist.

14. The composition of claim 1 , wherein the (co)polyester has an intrinsic viscosity from 1.3 deciliter/gram to 2.5 deciliter/gram.

15. The composition of claim 9 , wherein the polyethylene terephthalate has an intrinsic viscosity from 1.3 deciliter/gram to 2.5 deciliter/gram.