Method of making a photovoltaic device with antireflective coating
View Patent ↗A method of making an anti-reflection coating using a sol-gel process, for use in a photovoltaic device or the like. The method may include the following steps in certain example embodiments: forming a polymeric component of silica by mixing silane(s) with one or more of a first solvent, a catalyst, and water; forming a silica sol gel by mixing the polymeric component with a colloidal silica, and optionally a second solvent; forming a metal oxide sol by mixing silane(s) with a metal oxide, a second catalyst, and a third solvent; forming a combined sol by mixing the metal oxide sol with the silica sol; casting the mixture by spin coating or the like to form a silica and metal oxide containing layer on a substrate; and curing and/or heat treating the layer. This layer may make up all or only part of an anti-reflection coating which may be used in a photovoltaic device or the like.
1. A method of making a photovoltaic device including an antireflective coating, the method comprising:
forming a polymeric component of silica by mixing at least one silane with at least a first solvent, a first catalyst, and water;
forming a silica sol by mixing the polymeric component with a colloidal silica and a second solvent;
forming a metal oxide sol by mixing at least one silane with a metal oxide, a second catalyst, and a third solvent;
forming a combined sol gel by mixing the silica sol with the metal oxide sol;
casting the combined sol gel by spin coating to form a layer on a glass substrate;
curing and/or heat treating the layer, and using the resulting layer as at least part of an antireflective film on the glass substrate in a photovoltaic device.
2. A method of making a photovoltaic device including an antireflective coating, the method comprising:
forming a polymeric component of silica by mixing at least glycydoxypropyltrimethoxysilane with at least a first solvent, a first catalyst, and water;
forming a silica sol by mixing the polymeric component with a colloidal silica and a second solvent;
forming a metal oxide sol by mixing at least glycydoxypropyltrimethoxysilane with a metal oxide, a second catalyst, and a third solvent;
forming a combined sol gel by mixing the silica sol with the metal oxide sol;
casting the combined sol gel to form a layer on a glass substrate;
curing and/or heat treating the layer, and using the resulting layer as at least part of an antireflective film on the glass substrate in a photovoltaic device.
3. The method of claim 2 , wherein the curing is performed and occurs at a temperature between 100 and 150° C. and has a duration of no more than about 2 minutes.
4. The method of claim 2 , wherein the heat treating occurs and is at a temperature between 600 and 750° C. and has a duration of no greater than about 5 minutes.
5. The method of claim 2 , wherein (a) one or more of the first solvent, the second solvent, and the third solvent comprise n-propanol, and/or (b) the casting comprises spin coating.
6. The method of claim 2 , wherein the first catalyst and/or second catalyst comprise an acid.
7. The method of claim 6 , wherein the acid comprises hydrochloric acid.
8. The method of claim 2 , wherein the colloidal silica comprises methyl ethyl ketone.
9. The method of claim 2 , wherein the metal oxide sol further comprises a complex agent.
10. The method of claim 9 , wherein the complex agent comprises acetylacetate.
11. The method of claim 2 , wherein the combined sol gel comprises at least two metal oxide sols.
12. The method of claim 2 , wherein the metal oxide sol comprises at least 0.1 % wt of the combined sol gel.
13. The method of claim 12 , wherein the metal oxide sol comprises 1 to 5% wt of the combined sol gel.
14. The method of claim 13 , wherein the metal oxide sol comprises 2% wt of the combined sol gel.
15. The method of claim 2 , wherein the metal oxide comprises at least one metal oxide selected from aluminum tert butoxide and zirconium butoxide.
16. The method of claim 2 , wherein the metal oxide sol comprises at least one of 3Al 2 O 3 :2SiO 2 , Al 2 O 3 :SiO 2 , Mg Al 2 O 4 , ZrO 2 , Al 2 O 3 , and CaAl 2 Si 2 O 8 .
17. The method of claim 2 , wherein the metal oxide sol comprises at least one metal oxide having a refractive index (n) no greater than 2.0.
18. The method of claim 2 , wherein the metal oxide sol comprises at least one metal oxide having a refractive index (n) less than 2.0.