Acoustical panel and method of making such panel
View Patent ↗A lightweight acoustical panel having a substantially monolithic appearance and high sound absorption capabilities is manufactured at a lower cost than acoustical panels having comparable properties. The panel is formed, punched with pins and coated with a coarse particle coating.
1. A coated panel comprising:
a substrate having a thickness in the range from about 0.5 inches and 0.75 inches, a density in the range from about 1.25 to about 1.7 lbs/board foot and a porosity in the range from about 83.0% to about 90.0%; the substrate having perforations extending through a top surface thereof, the perforations being present in an amount from about 500 to about 1750 perforations per square foot, wherein the average perforation diameter is in the range from about 0.035 to about 0.055 inches;
a coating layer applied to the top surface of the substrate; and
a coarse particle layer applied on top of the coating layer, the coarse particle layer consisting essentially of coarse particles having an average particle size in the range from about 250 to about 750 microns, the coarse particle layer being present in an amount in the range from about 45 to about 80 grams per square foot;
wherein the coated panel has a noise reduction coefficient in the range from about 0.575 to about 0.725 and a light reflectance value in the range from about 0.82 to about 0.88.
2. The coated panel of claim 1 , wherein the substrate comprises from about 40% to about 85% fibrous filler, from about 4% to about 15% binder, from about 2% to about 10% cellulosic fibers, from 0% to about 50% expanded perlite, on a dry wt. % basis.
3. The coated panel of claim 1 , wherein said density of the substrate is in the range of about 1.30 to about 1.4 lb./bd. ft.
4. The coated panel of claim 2 , wherein the fibrous filler comprises mineral wool, fiberglass, rock wool, slag wool, and combinations thereof.
5. The coated panel of claim 2 , wherein said binder comprises granular starches, polystyrene, polyvinyl acetate, polystyrene acrylics, styrene butadiene, and combinations thereof.
6. The coated panel of claim 5 , wherein said granular starches comprise pearl starch, wheat starch, and potato starch.
7. The coated panel of claim 2 , wherein said panel further comprises non-fibrous fillers.
8. The coated panel of claim 7 , wherein said non-fibrous fillers comprises kaolin clay, calcium carbonate, silica, vermiculite, ball clay or bentonite, talc, mica, gypsum, and combinations thereof.
9. The coated panel of claim 1 , wherein the coating layer is present in an amount from about 17 to about 22 grams per square foot.