Heat treatable low-E coated articles and methods of making same by sputtering Ag in oxygen inclusive atmosphere
View Patent ↗A sputter coated article is provided with improved mechanical durability (e.g., pre-HT scratch resistance) and/or thermal stability by sputtering at least one Ag inclusive layer in an atmosphere including at least O 2 gas. For instance, in certain example embodiments an Ag inclusive target may be sputtered in an atmosphere including a combination of Ar and O 2 gas. In certain embodiments, this enables the resulting AgO x infrared (IR) reflecting layer to better adhere to adjacent contact layer(s).
1. A method of making a coated article including a coating supported by a substrate, the method comprising:
sputtering a first dielectric layer on the substrate;
sputtering a first contact layer over at least the first dielectric layer;
sputtering a target comprising Ag in an atmosphere including at least oxygen gas in order to form an infrared (IR) reflecting layer which is located over and contacts the first contact layer;
sputtering a second contact layer over and contacting the IR reflecting layer;
wherein said sputtering of at least one of the first and second contact layers comprises sputtering at least one target comprising a metal or metal alloy in an atmosphere including at least oxygen gas in order to form the contact layer(s) so as to comprise a metal oxide, and wherein more oxygen gas is introduced into said atmosphere in which the target for sputtering the contact layer(s) is located than is introduced into an atmosphere in which the target comprising Ag used in sputtering the IR reflecting layer is located; and
wherein a ratio of (a) oxygen gas introduced into said atmosphere in which the target comprising Ag used in sputtering the IR reflecting layer is located, to (b) oxygen gas introduced into the atmosphere in which the target for sputtering the contact layer(s) is located, is from about 1:1.3 to 1:10.
2. The method of claim 1 , wherein the at least one of the first and second contact layers comprising the metal oxide comprises an oxide of NiCr.
3. The method of claim 2 , wherein each of said first and second contact layers comprises an oxide of NiCr.
4. The method of claim 1 , wherein the ratio is from about 1:1.5 to 1:8.
5. The method of claim 1 , wherein the ratio is from about 1:2 to 1:5.
6. The method of claim 1 , wherein from about 20-100 sccm of oxygen gas is introduced into the atmosphere in which the target comprising Ag is located.
7. The method of claim 6 , wherein at least one of the contact layers comprises an oxide of Ni and/or Cr.
8. The method of claim 1 , wherein from about 20-60 sccm of oxygen gas is introduced into the atmosphere in which the target comprising Ag is located.
9. The method of claim 1 , wherein both the oxygen gas and argon gas are introduced into the atmosphere in which the target comprising Ag is located, and wherein more argon gas than oxygen gas is introduced into the atmosphere in which the target comprising Ag is located.
10. The method of claim 1 , wherein at least one of the contact layers comprises NiCrO x and is oxidation graded so that a first portion of said one contact layer close to said infrared (IR) reflecting layer is less oxidized than a second portion of said one contact layer that is further from said infrared (IR) reflecting layer.
11. The method of claim 1 , further comprising heat treating the glass substrate with the coating thereon in order to thermally temper the same, and wherein visible transmission of the coated article increases as a result of said heat treating.
12. The method of claim 1 , wherein the first dielectric layer comprises silicon nitride.
13. The method of claim 1 , further comprising sputtering a layer comprising tin oxide over the second contact layer.
14. The method of claim 1 , further comprising sputtering a layer comprising silicon nitride over the second contact layer, and then sputtering a second IR reflecting layer comprising silver over the layer comprising silicon nitride.
15. The method of claim 14 , further comprising sputtering another layer comprising silicon nitride over the second IR reflecting layer comprising silver.
16. The method of claim 15 , wherein a layer comprising tin oxide is located over the second IR reflecting layer so as to be provided between the second IR reflecting layer and the another layer comprising silicon nitride.