Barrier properties of substantially linear HDPE film with nucleating agents
View Patent ↗Disclosed is a method for improving the barrier properties of polyethylene films. The method comprises mixing a substantially linear, high density polyethylene with a nucleating agent and converting the mixture into a film. The film made by the method of the invention has at least a 15% improvement on the water vapor barrier property and/or in the oxygen barrier property compared with the control film made from the same substantially linear, high density polyethylene but does not contain the nucleating agent.
1. A method for improving the barrier properties of a polyethylene film, said method comprising the step of:
converting into a film a mixture comprising
a substantially linear, high density polyethylene (HDPE) having a long chain branching index (LCBI) less than or equal to 0.5 and a melt flow ratio (MFR) less than or equal to 65, and
a nucleating agent selected from the group consisting of glycerol alkoxide salts, hexahydrophthalic acid salts, and mixtures thereof,
wherein the nucleating agent is present in an amount within the range of about 0.01 wt. % to 1 wt. % of the weight of the substantially linear, high density polyethylene,
wherein the film has at least a 15% improvement, compared with a control film which is made from the same substantially linear HDPE but does not contain the nucleating agent, in the water vapor barrier property or in the oxygen barrier property.
2. The method of claim 1 , wherein the nucleating agent is a metal glycerolate selected from the group consisting of zinc glycerolates, magnesium glycerolates, calcium glycerolates, and mixtures thereof.
3. The method of claim 1 , wherein the nucleating agent is a zinc glycerolate.
4. The method of claim 1 , wherein the nucleating agent is a hexahydrophthalic acid metal salt selected from zinc hexahydrophthalate, magnesium hexahydrophthalate, calcium hexahydrophthalate, and mixtures thereof.
5. The method of claim 1 , wherein the nucleating agent is calcium hexahydrophthalate.
6. The method of claim 1 , wherein the substantially linear HDPE has an LCBI less than or equal to 0.3.
7. The method of claim 1 , wherein the substantially linear HDPE has an LCBI less than or equal to 0.2.
8. The method of claim 1 , wherein the substantially linear HDPE has an MFR less than or equal to 40.
9. The method of claim 1 , wherein the substantially linear HDPE has an MFR less than or equal to 20.
10. The method of claim 1 , wherein the substantially linear HDPE has a melt index (MI 2 ) within the range of 0.5 to 50 dg/min.
11. The method of claim 1 , wherein the substantially linear HDPE has a melt index (MI 2 ) within the range of 1 to 10 dg/min.
12. The method of claim 1 , wherein the film has at least a 25% improvement in the water vapor barrier property.
13. The method of claim 1 , wherein the film has at least a 45% improvement in the water vapor barrier property.
14. The method of claim 1 , wherein the film has at least a 25% improvement in the oxygen barrier property.
15. The method of claim 1 , wherein the film has at least a 45% improvement in the oxygen barrier property.
16. The method of claim 1 , wherein the film has at least a 45% improvement in the water barrier property and at least a 45% improvement in the oxygen barrier property.